Microstructure and Corrosion Behavior of Laser Welded Magnesium Alloys with Silver Nanoparticles

Magnesium alloys have gained increased attention in recent years in automotive, electronics, and medical industry. This because of magnesium alloys have better properties than aluminum alloys and steels in respects of their low density and high strength to weight ratio. However, the main problems of magnesium alloy welding are the crack formation and the appearance of porosity during the solidification. This paper proposes a unique technique to weld two thin sheets of AZ31B magnesium alloy using a paste containing Ag nanoparticles. The paste containing Ag nanoparticles of 5 nm in average diameter and an organic solvent was used to coat the surface of AZ31B thin sheet. The coated sheet was heated at 100 °C for 60 s to evaporate the solvent. The dried sheet was set as a lower AZ31B sheet on the jig, and then lap fillet welding was carried out by using a pulsed Nd:YAG laser in a closed box filled with argon gas. The characteristics of the microstructure and the corrosion behavior of the joints were analyzed by opticalmicroscopy (OM), energy dispersive spectrometry (EDS), electron probe micro-analyzer (EPMA), scanning electron microscopy (SEM), and immersion corrosion test. The experimental results show that the wrought AZ31B magnesium alloy can be joined successfully using Ag nanoparticles. Ag nanoparticles insert promote grain refinement, narrower the HAZ width and wider bond width compared to weld without and insert. Corrosion rate of welded AZ31B with Ag nanoparticles reduced up to 44 % compared to base metal. The improvement of corrosion resistance of welded AZ31B with Ag nanoparticles due to finer grains and large grain boundaries area which consist of high Al content. β-phase Mg17Al12 could serve as effective barrier and suppressed further propagation of corrosion. Furthermore, Ag distribution in fusion zone provide much more finer grains and may stabilize the magnesium solid solution making it less soluble or less anodic in aqueous Keywords—Laser welding, magnesium alloys, nanoparticles, mechanical property M. Ishak. is with the Faculty of Mechanical Engineering, University Malaysia Pahang, 26600 Pekan, Pahang, MALASYIA (phone: 60-9-4242332; fax: 60-9-424-2202; e-mail: mahadzir@ ump.edu.my). K.Yamasaki. is with Mechanical Engineering Department, Ibaraki University, Hitachi, 316-8511 Ibaraki, JAPAN. (e-mail: yamasaki@ mx.ibaraki.ac.jp). K.Maekawa is with the Mechanical Engineering Department, Ibaraki University, Hitachi, 316-8511 Ibaraki, JAPAN. (e-mail: [email protected]).