Anomalous enhancement in interfacial perpendicular magnetic anisotropy through uphill diffusion
نویسندگان
چکیده
We observed interfacial chemical sharpening due to uphill diffusion in post annealed ultrathin multilayer stack of Co and Pt, which leads to enhanced interfacial perpendicular magnetic anisotropy (PMA). This is surprising as these elements are considered as perfectly miscible. This chemical sharpening was confirmed through quantitative energy dispersive x-ray (EDX) spectroscopy and intensity distribution of images taken on high angle annular dark field (HAADF) detector in Scanning Transmission Electron Microscopic (STEM) mode. This observation demonstrates an evidence of miscibility gap in ultrathin coherent Co/Pt multilayer stacks.
منابع مشابه
How antiferromagnetism drives the magnetization of a ferromagnetic thin film to align out of plane.
Interfacial moments of an antiferromagnet are known for their prominent effects of induced coercivity enhancement and exchange bias in ferromagnetic-antiferromagnetic exchange-coupled systems. Here we report that the unpinned moments of an antiferromagnetic face-centered-cubic Mn layer can drive the magnetization of an adjacent Fe film perpendicular owing to a formation of intrinsic perpendicul...
متن کاملAnatomy and Giant Enhancement of the Perpendicular Magnetic Anisotropy of Cobalt-Graphene Heterostructures.
We report strongly enhanced perpendicular magnetic anisotropy (PMA) of Co films by graphene coating from both first-principles and experiments. Our calculations show that graphene can dramatically boost the surface anisotropy of Co films up to twice the value of its pristine counterpart and can extend the out-of-plane effective anisotropy up to unprecedented thickness of 25 Å. These findings ar...
متن کاملControl of magnetic anisotropy and magnetic patterning of perpendicular Co/Pt multilayers by laser irradiation
We report an approach to altering the magnetic properties of 111 textured Co/Pt multilayer films grown on sapphire 0001 substrates in a controlled way using single-pulse laser irradiation. The as-grown films reveal a strong perpendicular magnetic anisotropy induced by interfacial anisotropy. We show that laser irradiation can chemically mix the multilayer structure particularly at the interface...
متن کاملRapid thermal annealing study of magnetoresistance and perpendicular anisotropy in magnetic tunnel junctions based on MgO and CoFeB
The tunneling magnetoresistance and perpendicular magnetic anisotropy in CoFeB(1.1-1.2 nm)/ MgO/CoFeB(1.2-1.7 nm) junctions were found to be very sensitively dependent on annealing time. During annealing at a given temperature, decay of magnetoresistance occurs much earlier compared to junctions with in-plane magnetic anisotropy. Through a rapid thermal annealing study, the decrease of magnetor...
متن کامل