Modelling the surface free energy parameters of polyurethane coats—part 2. Waterborne coats obtained from cationomer polyurethanes

Polyurethane cationomer coats were synthesised on the basis of typical diisocyanates, properly selected polyether polyols, HO-tertiary amines and HCOOH as quaternisation reagents. The values of their surface free energy (SFE) parameters were obtained by the van Oss-Good method, with the use of the contact angle values which had been found by the goniometric method. Based on the obtained findings, empirical models were developed which made it possible to anticipate the effects of the raw material types on the SFE values of the produced coats. The possibility was noted to adjust the SFE values within 25-50 mJ/m2 by selecting carefully suitable parent substances. The principal consequences for the formation of improved hydrophobicity coats, applicable inter alia specialised protective coatings, were found to come not only from diisocyanate and polyol types but also from the alkylammonium cation structure which results from the use of different tertiary amines. The fundamental SFE lowering effect was noted when tertiary amines with 0-15 % of the 2,2,3,3-tetrafluoro-1,4-butanediol as a fluorinated chain extender was incorporated into polymer chains.