Sintering of Nd-Fe-B Magnets from Dy Coated Powder
نویسندگان
چکیده
High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundary. The maximum thickness of the Dy shell was approximately 70 nm. The maximum coercivity of the Dy sputter coated samples(sintered samples) increased from 1162.42 to 2020.70 kA/m. The microstructures of the (Nd,Dy)2Fe14B phases were effectively controlled, resulting in improved magnetic properties. The increase in coercivity of the Nd-Fe-B sintered magnet is discussed from a microstructural point of view.
منابع مشابه
Effect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets
Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...
متن کاملAn XMCD-PEEM study on magnetized Dy-doped Nd-Fe-B permanent magnets
on magnetized Dy-doped Nd-Fe-B permanent magnets R. Yamaguchi K. Terashima K. Fukumoto Y. Takada M. Kotsugi Y. Miyata K. Mima S. Komori S. Itoda Y. Nakatsu M. Yano N. Miyamoto T. Nakamura T. Kinoshita Y. Watanabe A. Manabe S. Suga S. Imada We have succeeded in developing a method for photoemission electron microscopy (PEEM) on fully magnetized ferromagnetic bulk samples and have applied this te...
متن کاملRAPID COMMUNICATION Nanocomposite (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer magnets with high performance
The structural and magnetic properties of rare-earth nanocomposite magnets of a (Nd,Dy)(Fe,Co,Nb,B)5.5 single layer and a (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer prepared by sputtering and heat treatment have been investigated. Incomplete exchange coupling behaviour is observed in the Ti-buffered NdDyFeCoNbB + 40 wt%Fe single layer magnet. After annealing, the laminated nanostructure consisting ...
متن کاملMagnetic Properties Improvement of Die-upset Nd-Fe-B Magnets by Dy-Cu Press Injection and Subsequent Heat Treatment
Ultrafine-grained die-upset Nd-Fe-B magnets are of importance because they provide a wide researching space to redesign the textured structures. Here is presented a route to obtain a new die-upset magnet with substantially improved magnetic properties. After experiencing the optimized heat treatment, both the coercivity and remanent magnetization of the Dy-Cu press injected magnets increased su...
متن کاملCoercivity enhancement of Nd-Fe-B sintered magnets by grain boundary modification via reduction-diffusion process
The interface between the Nd2Fe14B particles and the grain boundary surrounding them in Nd-Fe-B sintered magnets was modified by diffusion Dy metal selectively through the grain boundary involving the reduction of Dy2O3 or DyF3 with CaH2 and the coercivity of them was effectively enhanced from 0.98 MA/m to 1.42 MA/m with keeping the high value of remanence. The resultant coercivity was higher t...
متن کامل