An Antireflective Nanostructure Array Fabricated by Nanosilver Colloidal Lithography on a Silicon Substrate
نویسندگان
چکیده
An alternative method is presented for fabricating an antireflective nanostructure array using nanosilver colloidal lithography. Spin coating was used to produce the multilayered silver nanoparticles, which grew by self-assembly and were transformed into randomly distributed nanosilver islands through the thermodynamic action of dewetting and Oswald ripening. The average size and coverage rate of the islands increased with concentration in the range of 50-90 nm and 40-65%, respectively. The nanosilver islands were critically affected by concentration and spin speed. The effects of these two parameters were investigated, after etching and wet removal of nanosilver residues. The reflection nearly disappeared in the ultraviolet wavelength range and was 17% of the reflection of a bare silicon wafer in the visible range.
منابع مشابه
Fabrication and Optical Characterization of Silicon Nanostructure Arrays by Laser Interference Lithography and Metal-Assisted Chemical Etching
In this paper metal-assisted chemical etching has been applied to pattern porous silicon regions and silicon nanohole arrays in submicron period simply by using positive photoresist as a mask layer. In order to define silicon nanostructures, Metal-assisted chemical etching (MaCE) was carried out with silver catalyst. Provided solution (or materiel) in combination with laser interference lithogr...
متن کاملVersatile pattern generation of periodic, high aspect ratio Si nanostructure arrays with sub-50-nm resolution on a wafer scale
We report on a method of fabricating variable patterns of periodic, high aspect ratio silicon nanostructures with sub-50-nm resolution on a wafer scale. The approach marries step-and-repeat nanoimprint lithography (NIL) and metal-catalyzed electroless etching (MCEE), enabling near perfectly ordered Si nanostructure arrays of user-defined patterns to be controllably and rapidly generated on a wa...
متن کاملFabrication of non-close-packed arrays of colloidal spheres by soft lithography.
Ordered 2D non-close-packed sphere arrays with controllable lattice structures have been fabricated by using soft lithography based on the solvent-swelling and mechanical deformation behaviors of PDMS film. The figure shows an SEM image of the ordered quasi-one-dimensional parallel wires of silica spheres on a polymer-coated substrate.
متن کاملTitanium oxide film for the bottom antireflective layer in deep ultraviolet lithography.
Titanium oxide thin film, fabricated with tetraisopropyltitanate and oxygen by electron cyclotron resonance-plasma-enhanced chemical vapor deposition, is investigated as a potential candidate for the antireflective layer in KrF excimer laser (248-nm) lithography. The oxygen flow-rate dependence of the optical properties such as the refractive index (n) and the extinction coefficient (k) of the ...
متن کاملPlasmonic and silicon spherical nanoparticle antireflective coatings
Over the last decade, plasmonic antireflecting nanostructures have been extensively studied to be utilized in various optical and optoelectronic systems such as lenses, solar cells, photodetectors, and others. The growing interest to all-dielectric photonics as an alternative optical technology along with plasmonics motivates us to compare antireflective properties of plasmonic and all-dielectr...
متن کامل