Plasma damage effects on low-k porous organosilicate glass

نویسندگان

  • H. Ren
  • G. A. Antonelli
  • Y. Nishi
  • J. L. Shohet
چکیده

Damage induced in low-k porous organosilicate glass SiCOH dielectric films by exposure to an electron cyclotron resonance ECR plasma was investigated. The effects of charged-particle bombardment and vacuum ultraviolet radiation were separated. Flux measurements showed that the ECR plasma has a greater photon flux in the vacuum ultraviolet VUV range than in the UV range. Damage was measured by examining the surface potential and capacitance-voltage characteristics after exposure. It was found that during argon ECR plasma processing, 75% of the charge accumulation comes from ions at the surface, while 25% of the charge accumulation occurs from charge trapped within the bulk of the dielectric film. The charge accumulation can be modified by changing the bias voltage of the wafer chuck. UV exposure was shown to repair both sources of damage. Fourier transform infrared FTIR spectroscopy results showed no significant change except for Si– CH3 x bonds. It was found that both charged-particle bombardment and radiation from the ECR plasma damage these bonds. Ellipsometric measurements showed that both the dielectric thickness and the dielectric constant changed during plasma exposure. In addition, both plasma-induced swelling and UV-exposure shrinking effects were observed. The plasma-induced swelling occurs at the surface of the dielectric without changing the porosity of the dielectric, while UV-induced shrinking changes the porosity significantly. © 2010 American Institute of Physics. doi:10.1063/1.3506523

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of vacuum-ultraviolet irradiation on the dielectric constant of low-k organosilicate dielectrics

Articles you may be interested in Effects of plasma and vacuum-ultraviolet exposure on the mechanical properties of low-k porous organosilicate glass J. Bandgap measurements of low-k porous organosilicate dielectrics using vacuum ultraviolet irradiation Appl. Characteristics of ultra low-k nanoporous and fluorinated silica based films prepared by plasma enhanced chemical vapor deposition Plasma...

متن کامل

Effects of plasma and vacuum-ultraviolet exposure on the mechanical properties of low-k porous organosilicate glass

Articles you may be interested in Bandgap measurements of low-k porous organosilicate dielectrics using vacuum ultraviolet irradiation Appl. The effect of water uptake on the mechanical properties of low-k organosilicate glass Mechanism of plasma-induced damage to low-k SiOCH films during plasma ashing of organic resists Plasma damage effects on low-k porous organosilicate glass Short-ranged st...

متن کامل

Effects of vacuum-ultraviolet irradiation on copper penetration into low-k dielectrics under bias-temperature stress

Articles you may be interested in Effect of vacuum-ultraviolet irradiation on the dielectric constant of low-k organosilicate dielectrics Appl. Effects of plasma and vacuum-ultraviolet exposure on the mechanical properties of low-k porous organosilicate glass J. Bandgap measurements of low-k porous organosilicate dielectrics using vacuum ultraviolet irradiation Appl. The effects of plasma expos...

متن کامل

Effects of vacuum ultraviolet irradiation on trapped charges and leakage currents of low-k organosilicate dielectrics

Articles you may be interested in Effect of vacuum-ultraviolet irradiation on the dielectric constant of low-k organosilicate dielectrics Appl. Bandgap measurements of low-k porous organosilicate dielectrics using vacuum ultraviolet irradiation Appl. The effects of plasma exposure and vacuum ultraviolet irradiation on photopatternable low-k dielectric materials Effect of vacuum ultraviolet and ...

متن کامل

The effect of water uptake on the mechanical properties of low-k organosilicate glass

The effect of water uptake on the mechanical properties of low-k organosilicate glass Water uptake in porous low-k dielectrics has become a significant challenge for both back-end-of-line integration and circuit reliability. The influence of absorbed water on the mechanical properties of plasma-enhanced chemical-vapor-deposited organosilicate glasses (SiCOH) was investigated with nanoindentatio...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2010