Simulation of the concrete chloride NT build - 492 migration test Aix
نویسنده
چکیده
Corrosion of steel reinforcement is the major cause of deterioration in concrete structures, and carbon dioxide and especially chlorides are the main causes of damage. The rate at which chloride ions diffuse through concrete is a major determinant of the durability of structures. If chloride ions reach the vicinity of the rebar, the passive film around the steel can start to break down and the process of corrosion begins.
منابع مشابه
Durability of Self-compacting Lightweight Aggregate Concretes (LWSCC) as Repair Overlays
For rehabilitation of damaged concrete structures, the durability of repair overlay is a very important issue. Self-compacting concretes (SCC) are known as a suitable repair overlay materials. In this study, the durability of different self-compacting lightweight aggregate concretes (LWSCC) and effect of lightweight aggregate type on them is investigated. 3 mix designs of LWSCC containing three...
متن کاملEffect of Impressed Current on Bond Strength Between Steel Rebar and Concrete
The deterioration of bond strength between reinforcing steel and concrete as a result of impressed cathodic current with respect to the exposure time was investigated. A current in the magnitude of 3ma/ft2 (based on reinforcing rebar area) was used for a period of five years. Chemical analyses for sodium (Na+), potassium (K+) and chloride (Cl-) ions in concrete cylinders were performed as a fun...
متن کاملPrediction of the Chloride Resistance of Concrete Modified with High Calcium Fly Ash Using Machine Learning
The aim of the study was to generate rules for the prediction of the chloride resistance of concrete modified with high calcium fly ash using machine learning methods. The rapid chloride permeability test, according to the Nordtest Method Build 492, was used for determining the chloride ions' penetration in concrete containing high calcium fly ash (HCFA) for partial replacement of Portland ceme...
متن کاملDiscussion of the Evolution of the Chloride Migration Coefficient of Portland Cement Concrete Tested by the Rapid Chloride Migration (rcm) Test at Long-term Curing Periods up to 5 Years
Chloride-induced corrosion of reinforced concrete is one of the main deterioration mechanisms leading to shortening of the service life of concrete structures. Therefore, assessment of the resistance of concrete to chloride ingress plays an important role in predicting the service life of such structures. The Rapid Chloride Migration (RCM) test is one of the accelerated test methods commonly us...
متن کاملDetermination of Permeability of Concrete to Chloride Ions by Rapid Test Procedures
Methods which can be used to assess the chloride permeability of various types of concrete in a relatively short time are described. An electrical potential from 60-80 volt DC is applied either between a chloride solution ponded on a slab surface and the top of rebar mat, or between two faces at a core taken from a structure. The amount of chloride and sum of the electrical current which passes...