Plastic Deformation Induced by Nanoindentation Test Applied on ZrN/Si3N4 Multilayer Coatings
نویسندگان
چکیده
ZrN/Si3N4 multilayer coating that alternates with either nanocrystalline ZrN or amorphous Si3N4 interlayers was fabricated by reactively magnetron sputtering in an Ar-N2 mixture atmosphere. The thicknesses of the nanocrystalline ZrN and the amorphous Si3N4 interlayers are ~12.5 and 2.5 nm, respectively. The ZrN/Si3N4 coating exhibits a promoted hardness of 28.6 ± 1.2 GPa when compared to the binary ZrN. Microstructure evolution just underneath the nanoindentation impression of the ZrN/Si3N4 multilayer coating has been investigated. The result indicates that both ZrN nanograin rotations and plastic flow of the Si3N4 interlayers contribute to the permanent deformation of the multilayer coating induced by the nanoindentation. In addition, the introduction of the a-Si3N4 interlayers hinders both the initiation and propagation of microcracks when the multilayer coating was applied to the scratch test. The propagation deflection of the microcracks was observed attributed to the heterogenous interface, which produces the hardness promotion of the multilayer coating eventually.
منابع مشابه
Superhard nanocomposite coatings. From basic science toward industrialization*
A variety of superhard coatings with Vickers plastic hardness exceeding 40 GPa have been reported by several research groups during the last five years (for recent reviews see refs [1,2]). However, one has to distinguish between superhard nanocomposites, such as nc-TiN/a-Si3N4, nc-TiN/a-Si3N4/aand nc-TiSi2, nc-(Ti1-xAlx)N/a-Si3N4, nc-TiN/TiB2, ncTiN/BN, etc. where the high hardness originates f...
متن کاملCorrosion Behavior of Ti/TiN Multilayer Nanostructured Coatings Applied on AISI 316L by Arc-PVD Method in the Simulated Body Fluid
In this investigation, Ti/TiN nanolayer and TiN single layer coatings were coated on substrate of AISI 316L stainless steel by applying physical vapor deposition (PVD) using the type of cathodic arc evaporation (CAE). The evaluation of microstructure were carried out using x-ray diffraction (XRD), nanoindentation, atomic force microscopy (AFM) as well as scanning electron microscopy (SEM). Pola...
متن کاملA new X-ray method for residual stress evaluation in coatings
Transition metal nitride coatings films such as TiN or ZrN have been extensively studied for industrial applications. Residual stresses of the coatings generally affect the mechanical behaviour and the corrosion resistance and hence the performance of the product. The development of new, fast and simple methods for the assessment of residual stresses is then of great importance for coating tech...
متن کاملA practical guide for analysis of nanoindentation data.
Mechanical properties of biological materials are increasingly explored via nanoindentation testing. This paper reviews the modes of deformation found during indentation: elastic, plastic, viscous and fracture. A scheme is provided for ascertaining which deformation modes are active during a particular indentation test based on the load-displacement trace. Two behavior maps for indentation are ...
متن کاملRate-dependent serrated flow and plastic deformation in Ti45Zr16Be20Cu10Ni9 bulk amorphous alloy during nanoindentation.
The plastic deformation of Ti45Zr16Be20Cu10Ni9 bulk metallic glass has been investigated by nanoindentation performed with loads ranging from 10 to 200 mN in a wide range of loading rates. The plastic flow in the alloy exhibited conspicuous serrations at low loading rates. The serrations, however, became less prominent as the rate of indentation increased. Atomic force microscopy showed a signi...
متن کامل