Mechanical Characterization and Fractography of Pc, Abs and Pmma – a Comparison of Tensile, Impact and Esc Fracture Surfaces

This work presents an effort to document and describe fracture surfaces for three commercially available amorphous polymers (PC, PMMA and ABS) each subjected to tension, impact and environmental stress cracking (ESC). We present mechanical properties as well as microscopic characterization at low and high magnification to distinguish between slow tensile loading, fast impact loading, and environmentally assisted creep failure mechanisms. Chemical surface analysis of select fracture surfaces was also performed to evaluate its utility as a failure analysis technique for identifying ESC failure. The fractographic atlas presented herein serves to assist others in identifying topographical fracture surface features and crack growth mechanisms of failed plastic components, and more accurately distinguish between pure mechanical failure and ESC-generated fracture, where possible.