Wear Properties of Gabbro Based Glass and Glass-Ceramic Materials

Glass-ceramic materials were developed from gabbro including MgO and Al2O3 additives. Heat treatments for phase transformation from glassy matrix to glass-ceramic were carried out at 1000 ◦C for 3 h. X-ray di raction studies conducted on the glass-ceramic samples revealed that the phases formed in the glass-ceramics were cordierite, anorthite, diopsitic augite, forsterite and andesine. Glass and glass-ceramic materials were tested for wear properties against a harder alumina counterface using by a ball-on-disc tribometer at dry sliding condition. Wear tests were realized under the loads of 2.5, 5, and 7.5 N and at the sliding speeds of 0.1, 0.2, and 0.3 m/s. Wear rate of the glass and glass-ceramics ranged from 7.324× 10−7 and 2.150× 10−3 9.971× 10−7 and 4.982× 10−5 mm/m, respectively. It was shown that the crystallization treatment caused the decrease of wear rate.