Review on Thermo-Mechanical Fatigue Behavior of Nickel-Base Superalloys
نویسندگان
چکیده
Nickel-base superalloys have become the key materials of hot-end components in the aeroengines over the past several decades. Nickelbase superalloys are easy to produce thermo-mechanical fatigue (TMF) behavior when withstanding the combined effects of high temperature, creep, oxidation, mechanical stress and thermal stress. The occurrence of TMF seriously affects the normal service for hot-end components. Thus, the investigation about TMF behavior is of great significance. The TMF test can be divided into in-phase (IP) tests and out-of-phase (OP) tests. The fatigue life was described and compared for IP-TMF and OP-TMF. The reasons for various lives were analyzed. The classical life prediction models were evaluated. Cyclic stress response behaviors and hysteresis loops were analyzed. Cyclic deformation mechanism was revealed in depth. Fatigue fractographs of crack initiation and propagation were characterized on the fracture surfaces of fracture specimens. Crack initiation mechanism and fatigue damage mechanism were revealed in depth for TMF. [doi:10.2320/matertrans.M2015323]
منابع مشابه
Effect of bonding time on microstructure and mechanical properties during TLP bonding of nickel-base superalloys Hastelloy C276 and Stainless Steel AISI316
Joining of Hastelloy C276 nickel-base superalloy to AISI316 Stainless Steel using BNi-2 interlayer performed by transient liquid phase process (TLP) at 1150°C for 5 and 30 minutes. Bonding microstructure was studied using an Optical microscope and a scanning electron microscope (SEM). Vickers hardness test and shear strength test have been used to evaluate the mechanical properties. Microstruct...
متن کاملEffect of bonding time on microstructure and mechanical properties during TLP bonding of nickel-base superalloys Hastelloy C276 and Stainless Steel AISI316
Joining of Hastelloy C276 nickel-base superalloy to AISI316 Stainless Steel using BNi-2 interlayer performed by transient liquid phase process (TLP) at 1150°C for 5 and 30 minutes. Bonding microstructure was studied using an Optical microscope and a scanning electron microscope (SEM). Vickers hardness test and shear strength test have been used to evaluate the mechanical properties. Microstruct...
متن کاملMicrostructural aspects of fatigue in Ni-base superalloys.
Nickel-base superalloys are primarily used as components in jet engines and land-based turbines. While compositionally complex, they are microstructurally simple, consisting of small (50-1000 nm diameter), ordered, coherent Ni(3)(Al,Ti)-type L1(2) or Ni(3)Nb-type DO(22) precipitates (called γ(') and γ(''), respectively) embedded in an FCC substitutional solid solution consisting primarily of Ni...
متن کاملVacuum Levels Needed to Simulate Internal Fatigue Crack Growth in Titanium Alloys and Nickel-base Superalloys: Thermodynamic Considerations (preprint)
Prior studies have examined fatigue growth of surface cracks in vacuum to simulate sub-surface growth in Ti-alloys and Ni-base superalloys. Even with the highest vacuum level attained using “state-of-the-art” pumps, it is unclear if conditions of internal crack growth are truly simulated. We consider thermodynamics of the oxidation process to help answer this question. This consideration helps ...
متن کاملThermo-Mechanical Fatigue Crack Growth of RR1000
Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-is...