Low Temperature Vacuum Synthesis of Triangular CoO Nanocrystal/Graphene Nanosheets Composites with Enhanced Lithium Storage Capacity

CoO nanocrystal/graphene nanosheets (GNS) composites, consisting of a triangular CoO nanocrystal of 2~20 nm on the surface of GNS, are synthesized by a mild synthetic method. First, cobalt acetate tetrahydrate is recrystallized in the alcohol solution at a low temperature. Then, graphene oxide mixed with cobalt-precursor followed by high vacuum annealing to form the CoO nanocrystal/GNS composites. The CoO nanocrystal/GNS composites exhibit a high reversible capacity of 1481.9 m Ah g(-1) after 30 cycles with a high Coulombic efficiency of over 96% when used as anode materials for lithium ion battery. The excellent electrochemical performances may be attributed to the special structure of the composites. The well-dispersed triangular CoO nanocrystal on the substrate of conductive graphene can not only have a shorter diffusion length for lithium ions, better stress accommodation capability during the charge-discharge processes and more accessible active sites for lithium-ion storage and electrolyte wetting, but also possess a good conductive network, which can significantly improve the whole electrochemical performance.