Supporting Information Epitaxially Aligned Cuprous Oxide Nanowires for All-Oxide, Single-Wire Solar Cells
نویسندگان
چکیده
Fabrication of the single-wire solar cells Optical and electrical measurements Table S1: Electrical properties of the pristine and chlorine-exposed wires Table S2: Electrical properties of the ZnO deposited by low-temperature ALD Figure S1: XRD and facet identification of the chlorine-exposed wires
منابع مشابه
Epitaxially aligned cuprous oxide nanowires for all-oxide, single-wire solar cells.
As a p-type semiconducting oxide that can absorb visible light, cuprous oxide (Cu2O) is an attractive material for solar energy conversion. This work introduces a high-temperature, vapor-phase synthesis that produces faceted Cu2O nanowires that grow epitaxially along the surface of a lattice-matched, single-crystal MgO substrate. Individual wires were then fabricated into single-wire, all-oxide...
متن کاملNanowire-based all-oxide solar cells.
We present an all-oxide solar cell fabricated from vertically oriented zinc oxide nanowires and cuprous oxide nanoparticles. Our solar cell consists of vertically oriented n-type zinc oxide nanowires, surrounded by a film constructed from p-type cuprous oxide nanoparticles. Our solution-based synthesis of inexpensive and environmentally benign oxide materials in a solar cell would allow for the...
متن کاملChemical synthesis of oriented ferromagnetic LaSr-2 × 4 manganese oxide molecular sieve nanowires.
We report a chemical solution based method using nanoporous track-etched polymer templates for producing long and oriented LaSr-2 × 4 manganese oxide molecular sieve nanowires. Scanning transmission electron microscopy and electron energy loss spectroscopy analyses show that the nanowires are ferromagnetic at room temperature, single crystalline, epitaxially grown and self-aligned.
متن کاملHigh-performance transparent conducting oxide nanowires.
We report the growth and characterization of single-crystalline Sn-doped In2O3 (ITO) and Mo-doped In2O3 (IMO) nanowires. Epitaxial growth of vertically aligned ITO nanowire arrays was achieved on ITO/yttria-stabilized zirconia (YSZ) substrates. Optical transmittance and electrical transport measurements show that these nanowires are high-performance transparent metallic conductors with transmit...
متن کاملZnO Nanowires and Their Application for Solar Cells
Nanowires (NW) are defined here as metallic or semiconducting particles having a high aspect ratio, with cross-sectional diameters « 1 ┤m, and lengths as long as tens of microns. Well-aligned one-dimensional nanowire arrays have been widely investigated as photoelectrodes for solar energy conversion because they provide direct electrical pathways ensuring the rapid collection of carriers genera...