Spherical V-Fe-MCM-48: The Synthesis, Characterization and Hydrothermal Stability
نویسندگان
چکیده
Spherical MCM-48 mesoporous sieve co-doped with vanadium and iron was successfully synthesized via one-step hydrothermal method. The material was characterized by X-ray diffraction (XRD), nitrogen adsorption-desorption isotherms, inductively coupled plasma (ICP), scanning electron microscopy (SEM), transmission electron microscopy (TEM), diffuse reflectance UV-vis spectra, and X-ray photoelectron spectra (XPS) techniques. Results indicated that the V-Fe-MCM-48 showed an ordered 3D cubic mesostructure with spherical morphology, narrow pore size distribution and high specific surface area. Most of vanadium and iron atoms existing as tetrahedral V4+ and Fe3+ species were co-doped into the silicate framework. The particle sizes of V-Fe-MCM-48 were smaller and the specific area was much higher than those of of V-MCM-48. Additionally, the synthesized V-Fe-MCM-48 exhibited improved hydrothermal stability compared with the pure MCM-48.
منابع مشابه
Fe-MCM-22 catalyzed multicomponent synthesis of dihydropyrano [2,3-c] pyrazole derivatives
The Fe-MCM-22 zeolite was found to be an efficient solid heterogeneous catalyst for synthesis of dihydropyrano [2,3-c] pyrazoles via one pot four component reaction of ethyl acetoacetate, hydrazine hydrate, aromatic aldehyde and malononitrile in aqueous alcohol. The catalyst was synthesized by hydrothermal method under autogenous pressure and modified by Fe (III) ion exchange. The prepared cata...
متن کاملFe-MCM-22 catalyzed multicomponent synthesis of dihydropyrano [2,3-c] pyrazole derivatives
The Fe-MCM-22 zeolite was found to be an efficient solid heterogeneous catalyst for synthesis of dihydropyrano [2,3-c] pyrazoles via one pot four component reaction of ethyl acetoacetate, hydrazine hydrate, aromatic aldehyde and malononitrile in aqueous alcohol. The catalyst was synthesized by hydrothermal method under autogenous pressure and modified by Fe (III) ion exchange. The prepared cata...
متن کاملHighly Loaded Fe-MCM-41 Materials: Synthesis and Reducibility Studies
Fe-MCM-41 materials were prepared by different methods. The Fe was both incorporated into the structure and formed crystallites attached to the silica. High Fe content MCM-41 (~16 wt%) with retention of mesoporosity and long-range order was achieved by a range of new synthetic methodologies: (i) by delaying the addition of Fe(aq) to the stirred synthesis gel by 2 h, (ii) by addition of Fe precu...
متن کاملHYDROTHERMAL SYNTHESIS AND CHARACTERIZATION OF VANADIUM SILICATE MOLECULAR SIEVES WITH ANALCIME, MAGEDIITE AND ZSM-11 STRUCTURE
Vanadium silicates such as V-Al-analcime, V-analcime, V-magediite and V-ZSM-11 were synthesized using vanadium pentoxide or vanadyl sulfates. Vanadium silicates with analcime structure with and without aluminum (V-Al-analcime, V-analcime) were prepared as pure phase by hydrothermal crystallization from a gel with molar composition of (1 SiO2; 0.2 V2O5; 1 Na2O; 0.034 Al2O3; 35.7 H2O) and (1 SiO2...
متن کاملMicrowave–Assisted Hydrothermal Synthesis and Optical Characterization of SnO2 Nanoparticles
Semiconductor nanoparticles exhibit size dependent properties due to quantum confinement effect that are not present in their bulk counterparts. In this work, extremely fine and pure SnO2 nanoparticles of ~1.1 nm size were synthesized by a solution process, in which amorphous precipitate of SnO2 was crystallized by microwave heating. The particles sizes varied from ~1.1 to ~2.7 nm. By XRD analy...
متن کامل