Plasma-deposited fluoropolymer film mask for local porous silicon formation
نویسندگان
چکیده
The study of an innovative fluoropolymer masking layer for silicon anodization is proposed. Due to its high chemical resistance to hydrofluoric acid even under anodic bias, this thin film deposited by plasma has allowed the formation of deep porous silicon regions patterned on the silicon wafer. Unlike most of other masks, fluoropolymer removal after electrochemical etching is rapid and does not alter the porous layer. Local porous regions were thus fabricated both in p+-type and low-doped n-type silicon substrates.
منابع مشابه
Crystallization of amorphous silicon thin films deposited by PECVD on nickel-metalized porous silicon
Porous silicon layers were elaborated by electrochemical etching of heavily doped p-type silicon substrates. Metallization of porous silicon was carried out by immersion of substrates in diluted aqueous solution of nickel. Amorphous silicon thin films were deposited by plasma-enhanced chemical vapor deposition on metalized porous layers. Deposited amorphous thin films were crystallized under va...
متن کاملRF performances of inductors integrated on localized p+-type porous silicon regions
To study the influence of localized porous silicon regions on radiofrequency performances of passive devices, inductors were integrated on localized porous silicon regions, full porous silicon sheet, bulk silicon and glass substrates. In this work, a novel strong, resistant fluoropolymer mask is introduced to localize the porous silicon on the silicon wafer. Then, the quality factors and resona...
متن کاملFormation of Gold Microparticles by Ablation with Surface Plasmons
The formation of gold microparticles on a silicon substrate through the use of energetic surface plasmons is reported. A laser-assisted plasmonics system was assembled and tested to synthesize gold particles from gold thin film by electrical field enhancement mechanism. A mask containing an array of 200 nm diameter holes with a periodicity of 400 nm was prepared and placed on a silicon substrat...
متن کاملPorous Silicon Carbide for MEMS
Metal assisted photochemical etching (MAPCE) of 4H Silicon Carbide (SiC) was utilized to generate locally defined porous areas on single crystalline substrates. Therefore, Platinum (Pt) was sputter deposited on 4H-SiC substrates and patterned with photolithography and lift off. Etching was performed by immersing the Pt coated samples into an etching solution containing sodium persulphate and hy...
متن کاملThe Etching of Silicon Nitride in Phosphoric Acid with Silicon Dioxide as a Mask
The water content of phosphoric acid in etching silicon nitride and silicon dioxide plays an important role. An increase in water content increases the etch rate of silicon nitride and decreases the etch rate of silicon dioxide. The highest possible temperature for a fixed water content at atmospheric pressure in the system H2O-P2O5 is realized by boiling the liquid and refluxing the vapor phas...
متن کامل