Crack opening profile in DCDC specimen
نویسندگان
چکیده
The opening profile of the cracks produced in the Double Cleavage Drilled Compression (DCDC) specimens for brittle materials is investigated. The study is achieved by combining Finite Element simulations of a DCDC linear elastic medium with experimental measurements by crack opening interferometry on pure silica glass samples. We show that the shape of the crack can be described by a simple expression as a function of the geometrical parameters of the sample and the external loading conditions. This result can be used to measure accurately in real time relevant quantities during DCDC experiments, such as the crack length or the stress intensity factor applied to the specimen.
منابع مشابه
Fretting Fatigue with Cylindrical-On-Flat Contact: Crack Nucleation, Crack Path and Fatigue Life
Fretting fatigue experiments and finite element analysis were carried out to investigate the influence of cylindrical-on-flat contact on crack nucleation, crack path and fatigue life of medium-carbon steel. The location of crack nucleation was predicted using the maximum shear stress range criterion and the maximum relative slip amplitude criterion. The prediction using the maximum relative sli...
متن کاملNumerical Determination of Crack Opening and Closure Stress Intensity Factors
present work shows the numerical determination of fatigue crack opening and closure stress intensity factors of a C(T) specimen under variable amplitude loading using a finite element method. A half compact tension C(T) specimen, assuming plane stress constraint was used by finite element method covering the effects in two-dimensional (2D) small scale yielding models of fatigue crack growth und...
متن کاملNumerical Investigation on Stable Crack Growth in Plane Stress
Large deformation finite element analysis has been carried out to investigate the stress-strain fields ahead of a growing crack for compact tension (a/W=0.5) and three-point bend (a/W=0.1 and 0.5) specimens under plane stress condition. The crack growth is controlled by the experimental J-integral resistance curves measured by Sun et al. The results indicate that the distributions of opening st...
متن کاملEffect of Constraint on Ductile Crack Growth and Ductile-Brittle Fracture Transition of a carbon Steel
Ductile-brittle fracture transition was investigated using compact tension (CT) specimens from -70 o C to 40 o C for a carbon steel. Large deformation finite element analysis has been carried out to simulate the stable crack growth in the compact tension (CT, a/W=0.6), three point-point bend (SE(B), a/W=0.1) and centre-cracked tension (M(T), a/W=0.5) specimens. Experimental crack tip opening di...
متن کاملMonitoring fatigue crack growth and opening using antenna sensors
Fatigue cracking is one of the most common failure modes of various load-bearing structures. Even though sensors of many different types have been developed for crack detection, very few can monitor crack growth with a high sensitivity. This paper presents an antenna sensor that is capable of monitoring the growth of fatigue cracks with a sub-millimeter resolution. According to microstrip patch...
متن کامل