Temperature dependence of magnetoelastic properties of Fe100−xSix (5 < x < 20)

نویسندگان

  • G. Petculescu
  • P. K. Lambert
  • A. E. Clark
  • K. B. Hathaway
  • Qingfeng Xing
چکیده

Tetragonal magnetostriction (λγ,2) and elastic constants (c′, c44, and c11) for Fe100−xSixwere measured as a function of temperature (T). Compositions corresponding to the disordered A2 (x = 5), ordered D03 (x = 19.8), and mixed (x = 11.6) phases, were investigated. The magnetoelastic coupling (−b1) was determined for 77 < T < 300 K and compared with those of Fe-Ga, Fe-Ge, and Fe-Al. Both λγ,2(T) and −b1(T) of Fe-Si behave similarly to those of Fe-Ge, while other notable differences exist between the measured properties of Fe-Si and those of the other three alloys. Due to the early establishment of short range order, Fe-Si exhibits a positive, although small, slope in λγ,2(T) at 5 at. % Si, and a remarkable drop in −b1 before the solubility limit. The weaker softening of the tetragonal shear modulus with the addition of Si and the lack of strong anharmonic effects in the Fe-Si lattice inferred from the weak T-dependence of all the moduli suggest that FeSi exhibits more structural stability than the other three alloys. The distinctive behavior is likely due to the smaller size of Si compared to the sizes of Ga, Ge and Al, and therefore to the effect of the larger size difference between Fe and Si in the Fe-Si lattice.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

ساختار بلوری، خواص مغناطیسی و مغناطوالاستیکی ترکیب‌های بین فلزی Nd6Fe13-xCoxCu

Influence of the partial substitution of Co for Fe on the structural, magnetic and magnetoelastic properties of Nd6Fe13Cu compounds are investigated. Analysis of X-ray diffraction patterns indicates that the multi-phase sample is formed for all samples. Upon Co substitution, the second phase Nd2Fe17, Nd2Fe17-yCoy with 0 < y < 1 and Nd2Fe17-zCoz with 1 < z < 2 is formed in the samples with x = 0...

متن کامل

Magnetism and magnetic structures of PrMn2Ge2-xSix.

The structural and magnetic properties of seven PrMn2Ge2-xSix compounds with Si concentrations in the range x = 0.0-2.0 have been investigated by x-ray diffraction, magnetic (5-350 K), differential scanning calorimetry (300-500 K) and neutron diffraction (3-480 K) measurements. Replacement of Ge by Si leads to a contraction of the unit cell and significant modifications to the magnetic states--...

متن کامل

اثر جانشانی کبالت بر خواص مغناطوالاستیکی ترکیب Cu13Fe6Nd

In this research the magnetoelastic properties of Nd6Fe13­-x­­Co­xCu (x = 0 and 1) intermetallic compoundes are investigated. Analysis of X-ray diffraction patterns indicates that a single phase is formed approximately for x = 0 and the x = 1 sample is multi-phase. The lattice parameters were decreased, the Néel temperature of main phase and the Curie temperature of impurity phase was increased...

متن کامل

TRANSPORT AND MAGNETIC PROPERTIES OF (Fe100-xVx)75 P15C10 AMORPHOUS ALLOYS

(Fe100-xVx)75P15C10 (x = 0, 5, 10 and 15) amorphous alloys in the form of ribbon were prepared by the standard melt spinning technique and studied their transport and magnetic properties. The resistivity follows ‘Mooij correlation’ at low temperature (300 93) K. The Hall resistivity and the magnetoresistance (MR) were measured in an applied magnetic field up to 0.6T at room temperature (RT = 30...

متن کامل

Magnetic and magnetoelastic properties of Cr-substituted cobalt ferrite

Related Articles Electronic origin of the negligible magnetostriction of an electric steel Fe1-xSix alloy: A density-functional study J. Appl. Phys. 111, 063911 (2012) Modeling plastic deformation effect on magnetization in ferromagnetic materials J. Appl. Phys. 111, 063909 (2012) Magnetic and calorimetric studies of magnetocaloric effect in La0.7-xPrxCa0.3MnO3 J. Appl. Phys. 111, 07D726 (2012)...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2016