Hierarchically porous carbon monoliths with high surface area from bridged polysilsesquioxanes without thermal activation process.
نویسندگان
چکیده
Hierarchically porous carbon monoliths with high specific surface areas have been fabricated by removing nano-sized silica phase from carbon/silica composites pyrolyzed from bridged polysilsesquioxane. This activation method improves the homogeneity between inner and outer parts of the monoliths compared to the conventional thermal activation methods.
منابع مشابه
Synthesis of Porous Carbon Monoliths Using Hard Templates
The preparation of porous carbon monoliths with a defined shape via template-assisted routes is reported. Monoliths made from porous concrete and zeolite were each used as the template. The porous concrete-derived carbon monoliths exhibited high gravimetric specific surface areas up to 2000 m²·g-1. The pore system comprised macro-, meso-, and micropores. These pores were hierarchically arranged...
متن کاملThermally controlled growth of carbon onions within porous graphitic carbon-detonation nanodiamond monolithic composites
Copyright and Moral Rights for the articles on this site are retained by the individual authors and/or other copyright owners. For more information on Open Research Online's data policy on reuse of materials please consult the policies page. Unique porous carbon monoliths containing thermally annealed carbon onions, were prepared from a resorcinol formaldehyde precursor rod, containing silica g...
متن کاملSpontaneous preparation of hierarchically porous silica monoliths with uniform spherical mesopores confined in a well-defined macroporous framework.
Hierarchically porous silica monoliths with well-defined interconnected macropores and uniform spherical mesopores were spontaneously prepared by combining polymerization-induced phase separation with an epoxide-mediated sol-gel route without any complicated aging and drying and high-temperature heat treatment. The precise control of pore structures can be realized by using propylene oxide (PO)...
متن کاملDesign and Fabrication of Hierarchically Porous Carbon with a Template-free Method
Fabrication of hierarchically porous carbon materials (HPCs) with high surface area and pore volume has always been pursued. However, the currently effective template methods and acid/base activation strategies suffer from the drawbacks of either high costs or tedious steps. Herein, HPCs with 3D macro-mesopores and short-range meso-micropores were fabricated via an easy and sustainable two-step...
متن کاملUnprecedented CO2 uptake over highly porous N-doped activated carbon monoliths prepared by physical activation.
Highly porous N-doped activated carbon monoliths (ACMs) are fabricated by carbonization and physical activation of mesoporous polyacrylonitrile (PAN) monoliths in the presence of CO(2). The monoliths exhibit exceptionally high CO(2) uptake; 5.14 mmol g(-1) at ambient pressure and temperature and 11.51 mmol g(-1) at ambient pressure and 273 K.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 46 42 شماره
صفحات -
تاریخ انتشار 2010