Polymeric citrate precursor route to the synthesis of nano-sized barium lead titanates
نویسندگان
چکیده
Monophasic oxides of the formula, Ba!_xPbxTiO3 (0 < x < 1:0) were obtained at temperatures close to 500 8C from polymeric precursors formed using citric acid and ethylene glycol. These oxides were found to be tetragonal for all values of x, the distortion increasing with Pb content. Differential scanning calorimetry (DSC) shows that the decomposition of the precursor to the oxides varies with composition and the decomposition temperature is highest (530 8C) for thex = 0:5 composition. X-ray line broadening studies of 900 8C sintered samples show grain size of 50-54 nm in all compositions. TEM studies show agglomerated grains of the size, 40-60 nm. The dielectric constant (e) decreases with lead-doping having a value 70 for PbTiO3. The dielectric loss (D) for different compositions varied between 0.005 and 0.01 at 100 kHz. The dielectric constant and loss show excellent frequency stability.
منابع مشابه
Sonochemical Synthesis of Novel Nano Flower Lead(II) Metal-organic Coordination Polymer: A New Precursor to Produce Nano-sized PbO
Metal-organic coordination polymers are a class of organic–inorganic materials consists of metal ions linked together through multi-dentate organic ligands, to form a polymeric chain. These materials have received a great deal of attention in a wide range of different areassuch as catalysis, sensing, luminescence, separation and storage used . The new nano flowerPb(II) 1Dmetal-organic chain {[P...
متن کاملSonochemical Synthesis of a New Nano Lead(II) Coordination Polymer with 2,5-bis(2-pyridyl)-3,4-diaza-2,4- hexadiene ligand: A Precursor to Produce Pure Phase Nano- sized Lead(II) Oxide
A new nano-sized lead(II) coordination polymer, [Pb(2-bpdh)(NO3)2]n (1); (2-bpdh = 2,5-bis(2-pyridyl)-3,4-diaza-2,4-hexadiene)}, was synthesized by a sonochemical method. The structure of 1 may be considered coordination polymer of lead(II) consist of metallocyclicchains formed by bridging NO3- and 2-bpdh l...
متن کاملSonochemical Synthesis and Characterization of a Nano-Sized Lead (II) Coordination Polymer; A New Precursor for the Preparation of PbO Nanoparticles
Development of components that can form large molecular aggregates through non–covalent interactions, in nano size structures, has been an active area of research. In current study, a nano-sized Pb(II) coordination polymer, {[Pb(pydc)(pydc.H2)(H2O)2]2}n (1), where [pydc.H2= 2,6-pyridinedicarboxylic acid), wer...
متن کاملSynthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride
Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (T...
متن کاملSynthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride
Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (T...
متن کامل