A diffuse reflectance infrared Fourier-transform (DRIFT) study has been conducted at 373 K and 1 bar on an industrial Cr/Ti/SiO2 Phillips-type catalyst modified with, and without, triethylaluminium (TEAl) as co-catalyst. The reaction rate of the polymerization of ethylene, as monitored by the increase in the methylene stretching band of the growing polyethylene (PE), has been investigated as a function of the titanium content. After an initial period of mixed kinetics, with the reaction rate significantly higher for the TEAl-modified catalysts compared with the non-modified catalysts, the polymerization proceeded as a pseudo-zero-order reaction with a reaction rate that increased as a function of titanium loading. Furthermore, it was found that the higher Ti loading caused the appearance of more acidic hydroxyl groups and modified the Cr sites by making them more Lewis acidic, ultimately shortening the induction time and increasing the initial polymerization rate.
منابع مشابه
Phillips catalysts synthesized over various silica supports: Characterization and their catalytic evaluation in ethylene polymerization
Ethylene polymerization was carried out using Phillips chromium catalyst based on silica supports such as silica aerogel, SiO2 (Grace 643), and titanium modified SiO2 (G 643), and the results were compared with other catalysts based on SiO2 (Aldrich), SBA-15(Hex), SBA-15(Sp) and MCM-41. A combination of TGA, DSC, XRD, nitrogen adsorption, SEM, ICP, FTIR and other analyses were used to character...
متن کاملIntroduction of titanium species into fluorine-modified SiO2- supported Cr-V bimetallic catalyst for ethylene polymerization and ethylene/1-hexene copolymerization
Chromium-vanadium (Cr-V) bimetallic catalysts are prepared by the introduction of vanadium into the Phillips catalyst which is one of the most significant industrial ethylene polymerization catalysts for tuning the Phillips catalyst performances and improving polyethylene properties. In the present work, titanium species were introduced into the fluorine-modified chromium-vanadium bimetallic ca...
متن کاملPolyethylene with Reverse Co-monomer Incorporation: From an Industrial Serendipitous Discovery to Fundamental Understanding
A triethylaluminium(TEAl)-modified Phillips ethylene polymerisation Cr/Ti/SiO2 catalyst has been developed with two distinct active regions positioned respectively in the inner core and outer shell of the catalyst particle. DRIFTS, EPR, UV-Vis-NIR DRS, STXM, SEM-EDX and GPC-IR studies revealed that the catalyst produces simultaneously two different polymers, i.e., low molecular weight linear-ch...
متن کاملImido-modified SiO2-supported Ti/Mg Ziegler-Natta catalysts for ethylene polymerization and ethylene/1-hexene copolymerization
A novel imido-modified SiO2-supported Ti/Mg Ziegler-Natta catalyst for ethylene and ethylene/1-hexene polymerization is investigated. The catalyst is prepared by modification of (SiO2/MgO/MgCl2)TiClx Ziegler-Natta catalysts via supporting vanadium species followed by reaction with p-tolyl isocyanate as imido agents, to get the merits from both the SiO2-supported imido vanadium catalyst and the ...
متن کاملEffects of Ti/Mg molar ratio on bi-supported SiO2/MgCl2 (ethoxide type)/TiCl4 catalysts in ethylene homopolymerization and ethylene/1-hexene copolymerization
SiO2/MgCl2 (ethoxide type)/TiCl4 Ziegler-Natta catalysts for use in ethylene polymerization and ethylene/1-hexene copolymerization have been prepared using silica with a supported layer of magnesium ethoxide (Mg(OEt)2) as a catalyst precursor, followed by treating with TiCl4 at different Ti/Mg molar ratios, which showed significant effects on the active centers and pore structures of the cataly...