The aim of the present research was to fabricate and study crystal structure and phase composition of Bi5FeTi3O15 (BTFO) ceramics exhibiting Aurivillius type structure. By means of simultaneous thermal analysis and X-ray diffraction analysis the process of synthesis of BTFO ceramics has been studied. Mixed oxide method followed by pressureless sintering was used for ceramics preparation. Three endothermic thermal effects have been revealed on heating the stoichiometric mixture of initial powder oxides within the temperature range T = 700-1200 C, while only one strong endothermic peak was found on heating the powder after calcination. The weak endothermic peaks were ascribed to the melting points of intermediate surface phases based on Bi2O3-rich phase formed at low temperature. X-ray diffraction studies have shown that BFTO ceramics consisted of Bi5FeTi3O15 and Bi4Ti3O12 phases in amount of 88.3% and 11.7% (weight fraction), respectively. © 2017 Portuguese Society of Materials (SPM). Published by Elsevier España, S.L.U.. All rights reserved.
منابع مشابه
Sol-Gel Synthesis, Characterization and Optical Properties of Bi 3+ - Doped CdO Sub-Micron Size Materials
Highly crystalline Bi3+-doped cadmium oxide (CdO) sub-micron structures were synthesized by calcination the obtained precursor from a sol-gel reaction. The reaction was carried out with cadmium nitrate (Cd(NO3)2.4H2O), bismuth nitrate (Bi(NO3)3.5H2O) and ethylene glycol (C2H6O2) reactan...
متن کاملPreparation and Study of Bismuth Oxide Doped and co-Doped with Cobalt(III) and Holmium(III) via Sol-Gel Method
In this research work the solid-solutions of (Bi2O3)1-x (Co2O3)x, [x= 0.05, 0.1] (1), (Bi2O3)1-x (Ho2O3) x, [x= 0.025, 0.05] (2), and (Bi2O3)1-x-y (Co2O3)x (Ho2O3)y</su...
متن کاملSynthesis of Peculiar Structure of Hydroxyapatite Nanorods by Hydrothermal Condition for Biomedical Applications
In the present work, the effect of Ca(NO3)2.4H2O and (NH4)2HPO4 primary solutions as the beginning materials in synthesis of a calcium phosphate phase, was examined. So, we investigated the wet chemical reactions in solution at different temperatures by a hydrothermal condition aimed at hydroxyapatite (Ca10(PO<su...
متن کاملInfluence of Calcination Kinetics Parameters on Synthesis of KNN Piezoelectric Ceramics
The current research was focused on synthesizing potassium sodium niobate (KNN) piezoelectric ceramics for the system (K0.48Na0.52) NbO3 by high energy ball milling process for 15h at the speed of 300 rpm. The blended nano-crystalline powder was calcined in conventional box furnace at 700oC, 800oC and 900oC for duration of 5h, 7h and 10h. Diffraction result of calcine powder confirmed the f...
متن کاملKaolin-SO3H nanoparticles: A new efficient and reusable catalyst for synthesis of 2-substituted benzimidazoles at room temperature
Kaolinite clay found its application in medicine, in toothpaste, in cosmetic and as a food additive. Recently, a specially formulated spray is used in fruit and vegetable production to repel the insects and prevent sunburn. Kaolin-SO3H nanoparticles were prepared via reaction of kaolin and chlorosulfonic acid and characterized by FT-IR, XRD, FESEM, TEM, XRF, EDS, BET and TGA. 2-Substituted benz...
متن کامل