Glass formation in a (Ti,Zr,Hf)–(Cu,Ni,Ag)–Al high-order alloy system by mechanical alloying

نویسندگان

  • L C. Zhang
  • Z Q. Shen
  • Jian Xu
  • L. C. Zhang
  • Z. Q. Shen
  • J. Xu
چکیده

In this work, glass formation under high-energy ball milling was investigated for a (Ti0.33Zr0.33Hf0.33)50(Ni0.33Cu0.33Ag0.33)40Al10 high-order alloy system with equiatomic substitution for early and late transition-metal contents. For comparison, an amorphous alloy ribbon with the same composition was prepared using the melt-spinning method as well. Structural features of the samples were characterized using x-ray diffraction, transmission electron microscopy, and differential scanning calorimetry. Mechanical alloying resulted in a glassy alloy similar to that obtained by melt spinning. However, the glass formation was incomplete, and a small amount of unreacted crystallites smaller than 30 nm in size still remained in the final ball-milled product. Like the melt-spun glass, the ball-milled glassy alloy also exhibited a distinct glass transition and a wide supercooled liquid region of about 80 K. Crystallization of this high-order glassy alloy proceeded through two main stages. After the primary nanocrystallization was completed, the remaining amorphous phase also behaved as a glass, showing a detectable glass transition and a large supercooled liquid region of about 100 K.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Glass Formation, Chemical Properties and Surface Analysis of Cu-Based Bulk Metallic Glasses

This paper reviews the influence of alloying elements Mo, Nb, Ta and Ni on glass formation and corrosion resistance of Cu-based bulk metallic glasses (BMGs). In order to obtain basic knowledge for application to the industry, corrosion resistance of the Cu-Hf-Ti-(Mo, Nb, Ta, Ni) and Cu-Zr-Ag-Al-(Nb) bulk glassy alloy systems in various solutions are reported in this work. Moreover, X-ray photoe...

متن کامل

Effect of Ni on Amorphization of Ti-Cu-Ni Ternary alloys Prepared by Mechanical alloying

Amorphous alloys has been taken into consideration because of their unique properties and are nominated as the future engineering materials. In this research, the effect of Ni and milling time on amorphization process and thermal stability of Ti50Cu50-xNix(x=10, 15, 25 at%) alloy system were investigated. The evolution of amorphization during milling, thermal stability and subsequent heat treat...

متن کامل

Ti-based Bulk Metallic Glasses for Biomedical Applications

Biomedical materials can improve the life quality of a number of people each year. The range of applications includes such as joint and limb replacements, artificial arteries and skin, contact lenses, and dentures. So far the accepted biomaterials include metals, ceramics and polymers. The metallic biomaterials mainly contain stainless steel, Co-Cr alloys, Titanium and Ti-6Al-4V. Recently, bulk...

متن کامل

Combinatorial development of antibacterial Zr-Cu-Al-Ag thin film metallic glasses

Metallic alloys are normally composed of multiple constituent elements in order to achieve integration of a plurality of properties required in technological applications. However, conventional alloy development paradigm, by sequential trial-and-error approach, requires completely unrelated strategies to optimize compositions out of a vast phase space, making alloy development time consuming an...

متن کامل

Effect of Minor Alloying Substitution on Glass-Forming Ability and Crystallization Behavior of a Ni57Zr22X8Nb8Al5 (X=Ti, Cu) Alloy Synthesized by Mechanical Alloying

Ni57Zr22X8Nb8Al5 (X = Ti, Cu) metallic glass (MG) and nanocomposite powders were synthesized by mechanical alloying. Outstanding differences in glass-forming ability (GFA), thermal property, particle size and crystallization behavior were found for the two synthesized alloy powders with different alloying substitutions. The Ti-containing MG powder exhibits better GFA, higher thermal stability, ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2003