Nanofibrous Chitosan-Polyethylene Oxide Engineered Scaffolds: A Comparative Study between Simulated Structural Characteristics and Cells Viability
نویسندگان
چکیده
3D nanofibrous chitosan-polyethylene oxide (PEO) scaffolds were fabricated by electrospinning at different processing parameters. The structural characteristics, such as pore size, overall porosity, pore interconnectivity, and scaffold percolative efficiency (SPE), were simulated by a robust image analysis. Mouse fibroblast cells (L929) were cultured in RPMI for 2 days in the presence of various samples of nanofibrous chitosan/PEO scaffolds. Cell attachments and corresponding mean viability were enhanced from 50% to 110% compared to that belonging to a control even at packed morphologies of scaffolds constituted from pores with nanoscale diameter. To elucidate the correlation between structural characteristics within the depth of the scaffolds' profile and cell viability, a comparative analysis was proposed. This analysis revealed that larger fiber diameters and pore sizes can enhance cell viability. On the contrary, increasing the other structural elements such as overall porosity and interconnectivity due to a simultaneous reduction in fiber diameter and pore size through the electrospinning process can reduce the viability of cells. In addition, it was found that manipulation of the processing parameters in electrospinning can compensate for the effects of packed morphologies of nanofibrous scaffolds and can thus potentially improve the infiltration and viability of cells.
منابع مشابه
Perspectives of chitosan nanofiber/film scaffolds with bone marrow stromal cells in tissue engineering and wound dressing
Objective (s): Several methods have been proposed for repairing defects and damages, one of which is cell therapy. Bone marrow stromal cells seem to be suitable for this purpose. On the other hand, many biometric materials are used to improve and correct the defects in the body. Nanofibers are widely used in the medical industry, especially in tissue engineering, as scaffolds in wound healing a...
متن کاملImproved cellular infiltration into nanofibrous electrospun cross-linked gelatin scaffolds templated with micrometer-sized polyethylene glycol fibers.
Gelatin-based nanofibrous scaffolds with a mean fiber diameter of 300 nm were prepared with and without micrometer-sized polyethylene glycol (PEG) fibers that served as sacrificial templates. Upon fabrication of the scaffolds via electrospinning, the gelatin fibers were crosslinked with glutaraldehyde, and the PEG templates were removed using tert-butanol to yield nanofibrous scaffolds with por...
متن کاملDevelopment of Electrospun Chitosan-Polyethylene Oxide/Fibrinogen Biocomposite for Potential Wound Healing Applications
Normal wound healing is a highly complex process that requires the interplay of various growth factors and cell types. Despite advancements in biomaterials, only a few bioactive wound dressings reach the clinical setting. The purpose of this research was to explore the feasibility of electrospinning a novel nanofibrous chitosan (CS)-fibrinogen (Fb) scaffold capable of sustained release of plate...
متن کاملSynthesis and characterization of electrospun polyvinyl alcohol nanofibrous scaffolds modified by blending with chitosan for neural tissue engineering
Among several attempts to integrate tissue engineering concepts into strategies to repair different parts of the human body, neuronal repair stands as a challenging area due to the complexity of the structure and function of the nervous system and the low efficiency of conventional repair approaches. Herein, electrospun polyvinyl alcohol (PVA)/chitosan nanofibrous scaffolds have been synthesize...
متن کاملFabrication of Chitosan-Polyethylene Oxide Electrospun Nanofibrous Mats Containing Green Tea Extract
Novel electrospun nanofibrous CS-PEO nerve conduits containing 0, 2.5 and 5% of green tea methanolic extract were developed and characterized by FE-SEM, FT-IR, TGA/DSC as well as tensile strength analysis. The FE-SEM images revealed that all of the nanofibers had an average diameter of ∼80nm. The swelling degree was decreased by increasing the GT amount from 2.5 to 5% and this might be attribut...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
دوره 2014 شماره
صفحات -
تاریخ انتشار 2014