Effects of hydrothermal aging on glass–fiber/polyetherimide (PEI) composites

نویسندگان

  • Taner Yilmaz
  • Tamer Sinmazcelik
چکیده

The moisture absorption behavior and the influence of moisture on thermal and mechanical properties of glass–fiber/polyetherimide (PEI) laminates have been investigated. The laminates were exposed to hydrothermal aging at two different temperatures and high moisture rates. The properties of as-received and hydrothermally aged samples were compared. The hydrothermally aged laminates contained a large amount of moisture which caused decrease in the glass transition temperature and deterioration in mechanical properties (interlaminar shear strength, flexural modulus, bearing strength, etc.). Fractographic analysis revealed interfacial debonding as the dominant failure mechanism, indicating a strong influence of water degradation on fracture toughness results. Alterations in viscoelastic properties of glass/PEI composite which was exposed to hydrothermal aging were analyzed with the dynamic mechanical thermal analysis (DMTA) method. DMTA tests give evidence of plasticization of the PEI matrix.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Environmental effects on mechanical properties of glass/epoxy and fiber metal laminates, Part II: Isothermal aging

The aim of this study is to investigate effects of isothermal aging on mechanical properties of fiber metal laminates (FMLs) and glass/epoxy composites. For this purpose, both materials were fabricated using the wet lay-up manufacturing technique under vacuum pressure. Both the glass/epoxy composites and the FML specimens were then subjected to isothermal aging (130°C, dried air) for up to 5 we...

متن کامل

Environmental Effects on Mechanical Properties of Glass/Epoxy and Fiber Metal Laminates, Part I: Hygrothermal Aging

In this article, the effect of hygrothermal aging on mechanical properties of fiber metal laminates (FMLs) and E-glass/epoxy (GE) composites is investigated. First, FML and GE specimens were built using wet lay-up technique under vacuum pressure. Hygrothermal aging simulation was then carried out on both specimen types in distilled water at a constant temperature of 90 °C for 5 weeks. The resul...

متن کامل

A Comparative Study on the Application of Porous PES and PEI Hollow Fiber Membranes in Gas Humidifcation Process

Humidification process is one of the applications of membrane contactor in which partial pressure of a vapor in the gas stream increases. In this study, two different polyethersulfone and polyetherimide hollow fiber membranes were fabricated and characterized by various test methods and their performance in humidification process under different operating conditions was investigated. The PES me...

متن کامل

Developing the dielectric mechanisms of polyetherimide/multiwalled carbon nanotube/(Ba0.8Sr0.2)(Ti0.9Zr0.1)O3 composites

Various amounts of multiwalled carbon nanotubes [MWNTs] were embedded into polyetherimide [PEI] to form PEI/MWNT composites, and their dielectric properties were measured at 1 MHz. The Lichtenecker mixing rule was used to find a reasonable dielectric constant for the MWNTs used in this study. The dielectric constants of the developed composites were significantly increased, and the loss tangent...

متن کامل

Fabrication of Crosslinkable Hollow Fiber Membranes for Pervaporation Dehydration

Integrally-skinned asymmetric Polyetherimide/Poly (vinyl alcohol) (PEI/PVA) hollow fber membranes for pervaporation dehydration were fabricated by non-solvent induced phase inversion. PVA inside the PEI matrix could be crosslinked to provide membrane performance stability during long term operation. The effects of different PEI/PVA blend ratio, external coagulant type and...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2009