Multifunctional fiberglass-reinforced PMMA-BaTiO3 structural/dielectric composites

Fiberglass-reinforced polymer composites were investigated for potential use as structural dielectrics in multifunctional capacitors that require simultaneous excellent mechanical properties and good energy storage characteristics. Composites were fabricated employing poly(methyl methacrylate), PMMA, as the structural matrix. While barium titanate (BaTiO3) nanopowder was added to the composites for its high room temperature dielectric constant, fiberglass was employed to confer high stiffness. A conductive polymer blend of poly (3,4-ethylenedioxythiophene) and polystyrene sulfonate (PEDOT:PSS) was used to coat the BaTiO3 nanoparticles with the purpose of further elevating the dielectric constant of the resultant PMMA-composites. FTIR spectroscopy, TGA and SEM measurements were conducted to prove the successful coating of BaTiO3 nanoparticles with the PEDOT:PSS blend. TEM measurements revealed a good dispersion of coated nanoparticles throughout the PMMA matrix. The fiberglass-reinforcedPMMA composites containing neat and coated BaTiO3 were found to exhibit excellent stiffness. In addition, the use of PEDOT:PSS in conjunction with BaTiO3 was observed to improve the dielectric constant of the composites. Finally, the dielectric constant of the structural composites was found to vary only slightly with temperature. 2011 Elsevier Ltd. All rights reserved.