Effect of copper on precipitation and baking hardening behavior of Al−Mg−Si alloys
نویسندگان
چکیده
The effects of copper on the ageing precipitation behavior of as-quenched and pre-aged AA6016 aluminum alloy were studied by differential scanning calorimetry (DSC), Vickers hardness measurement and transmission electronic microscopy (TEM). The results indicate that the addition of copper facilitates the growth of clusters (GP I) to the critical size during pre-ageing. Therefore, the addition of copper accelerates the transition from GP I (pre-β′′) to GP II (β′′) during final artificial ageing, and finally results in the favorable paint-bake response. However, the one with the copper level of 0.3% does not show significant baking hardening response as expected. Pre-aging can also reduce the detrimental effect due to natural aging of copper-containing alloys.
منابع مشابه
THE EFFECT OF AGING ON THE CLUSTERING AND PRECIPITATION PROCESS IN Al-Mg-Si ALLOYS
The dependence of the mechanism of age hardening in Al-Mg-Si alloys on their Si content, the pre-aging conditions and addition of Cu has been investigated. For this purpose, the solute clusters and the metastable precipitates in aged Al-Mg-Si alloys have been characterized by a three dimensional atom probe (3DAP) and transmission electron microscopy (TEM). Atom probe analysis results have revea...
متن کاملStudy of the Precipitation Hardening Behaviour and Intergranular Corrosion of Al-Mg-Si Alloys with Differing Si Contents
The effects of Si addition on the precipitation hardening behaviour and evolution of intergranular corrosion (IGC) of Al-Mg-Si alloys were investigated using hardness tests, scanning electron microscopy (SEM), potentiodynamic polarization measurements, and high-resolution transmission electron microscopy (HRTEM). With an increase of the Si content, the peak hardness of the Al-Mg-Si alloys consi...
متن کاملFRACTIONAL RECRYSTALLIZATION KINETICS IN DIRECTLY COLD ROLLED Al-Mg, Al-Mg-Sc AND Al-Mg-Sc-Zr ALLOY
The evaluation of texture as a function of recrystallization has been characterized for directly cold rolled Al-6Mg, Al-6Mg-0.4Sc and Al-6Mg-0.4Sc-0.2Zr alloys. Samples were annealed isothermally at 400 °C for 1 to 240 minutes to allow recrystallization. Recrystallization kinetics of the alloys is analyzed from the micro-hardness variation. Isothermally annealed samples of aluminum alloys were ...
متن کاملThe Effect of Cu Additions on the Precipitation Kinetics in an Al-Mg-Si Alloy with Excess Si
The microstructural evolution during age hardening of a Cu-bearing Al-Mg-Si alloy has been investigated by the three-dimensional atom probe (3DAP) and transmission electron microscope (TEM) techniques, in order to clarify the effect of Cu on the initial age-hardening response. After 30 minutes of artificial aging at 175 8C, the alloy shows a significant increase in hardness. The TEM observation...
متن کامل