Band offsets and Fermi level pinning at metal-Al2O3 interfaces
نویسندگان
چکیده
Disparities between the predicted and the measured effective work functions (EWFs) in advanced metal oxide semiconductor devices, or Fermi-level pinning (FLP), have gained significant attention when high-k dielectrics began to emerge. Using a systematic approach for EWF extraction, combined with a comparison to unpinned SiO2 references, it was found that no intrinsic FLP exists in the model dielectric Al2O3. Extrinsic FLP was found with one of the metals investigated Ta, where a 0.4 eV increase in the EWF was observed in the electrical characteristics and confirmed by backside spectroscopy. The physical origins of the band offsets related to the EWF increase have been analyzed in detail. A 2-nm interfacial layer at the Ta-Al2O3 interface has been found and is suggested as the source of extrinsic FLP. Interfacial dipoles originating from Ta-O chemical bonds are considered as the mechanism responsible for the band offset. The results of this model system are then used to explain some of the peculiarities occurring at complex devices which are used in technological applications.
منابع مشابه
Defective Heterojunction Models
Fermi-level pinning behavior has been observed at the free surface, oxide interface, metal interface, MBE grown surface, stop-regrown homojunction, and misfit-dislocation pinned heterojunction of GaAs. Theories of such behavior are numerous and disparate. Theories of ideal heterojunction band offsets are less diverse, but have still not converged to a single mechanism. Recent studies of heteroj...
متن کاملOrigin of Fermi-level pinning at GaAs/oxide interfaces through the hybrid functional study of defects
Gallium arsenide is currently under scrutiny for replacing silicon in microelectronic devices due to its high carrier mobilities. However, the widespread use of this semiconductor is hampered by the intrinsic difficulty of producing high-quality interfaces with oxides. Indeed, proper device operation is generally prevented by a high density of interface defect states which lead to Fermi-level p...
متن کاملFermi-Level Pinning by Misfit Dislocations at GaAs Interfaces
Fermi-level pinning by misfit dislocations at GaAs interfaces has been investigated. n -GaInAs was used to control the misfit dislocation density by varying of composition and epilayer thickness. interfaces with zero or low dislocation densities are Ohmic to current flow, and become rectifying with increasing dislocation density. The "Schottky barrier height" increases with dislocation density ...
متن کاملThe unusual mechanism of partial Fermi level pinning at metal-MoS2 interfaces.
Density functional theory calculations are performed to unravel the nature of the contact between metal electrodes and monolayer MoS2. Schottky barriers are shown to be present for a variety of metals with the work functions spanning over 4.2-6.1 eV. Except for the p-type Schottky contact with platinum, the Fermi levels in all of the studied metal-MoS2 complexes are situated above the midgap of...
متن کاملSchottky-barrier height modulation of metal/In0.53Ga0.47As interfaces by insertion of atomic-layer deposited ultrathin Al2O3
The improvement of the metal/InGaAs interface is essential for the future application of InGaAs metal source/drain Schottky-barrier metal-oxide-semiconductor field-effect-transistors. In this article, on In0.53Ga0.47As, the authors examine the recently proposed method of inserting an ultrathin insulator to modulate the effective Schottky-barrier height SBH at the metal/semiconductor interface. ...
متن کامل