Improved Resistance Switching Stability in Fe-Doped ZnO Thin Films Through Pulsed Magnetic Field Annealing
نویسندگان
چکیده
Five percent of Fe-doped ZnO (ZnO:Fe) thin films were deposited on Pt/TiO2/SiO2/Si substrates by a spin-coating method. The films were annealed without (ZnO:Fe-0T) and with a pulsed magnetic field of 4 T (ZnO:Fe-4TP) to investigate the magnetic annealing effect on the resistance switching (RS) behavior of the Pt/ZnO:Fe/Pt structures. Compared with the ZnO:Fe-0T film, the ZnO:Fe-4TP film showed improved RS performance regarding the stability of the set voltage and the resistance of the high resistance state. Transmission electron microscopy and X-ray photoelectron spectroscopy analyses revealed that the ZnO:Fe-4TP film contains more uniform grains and a higher density of oxygen vacancies, which promote the easier formation of conducting filaments along similar paths and the stability of switching parameters. These results suggest that external magnetic fields can be used to prepare magnetic oxide thin films with improved resistance switching performance for memory device applications.
منابع مشابه
Correlation between crystal structure and optical properties of copper- doped ZnO thin films
ZnO and Cu doped[1] (CZO) thin films were prepared by radio frequency sputtering. The structural and optical properties of thin films were investigated using X-ray diffraction (XRD), atomic force microscopy (AFM), optical spectrophotometer, and photoluminescence (PL) techniques. ZnO thin films showed crystalline and micro-stress defects in the crystal lattice. Annealing of CZO thin films increa...
متن کاملProperties and Sensor Performance of Zinc Oxide Thin Films
Reactively sputtered ZnO thin film gas sensors were fabricated onto Si wafers. The atmosphere dependent electrical response of the ZnO micro arrays was examined. The effects of processing conditions on the properties and sensor performance of ZnO films were investigated. Using AFM, SEM, XRD and WDS, the O2/Ar ratios during sputtering and Al dopant were found to control the property of ZnO films...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کاملComparative studies of Al-doped ZnO and Ga-doped ZnO transparent conducting oxide thin films
We have investigated the influences of aluminum and gallium dopants (0 to 2.0 mol%) on zinc oxide (ZnO) thin films regarding crystallization and electrical and optical properties for application in transparent conducting oxide devices. Al- and Ga-doped ZnO thin films were deposited on glass substrates (corning 1737) by sol-gel spin-coating process. As a starting material, AlCl3⋅6H2O, Ga(NO3)2, ...
متن کامل