Wettability of denture relining materials under water storage over time

نویسندگان

  • Na-Young Jin
  • Ho-Rim Lee
  • Heesu Lee
  • Ahran Pae
چکیده

STATEMENT OF PROBLEM Poor wettability of denture relining materials may lead to retention problems and patient discomfort. PURPOSE Purpose of this study is to compare and evaluate wettability of nine denture relining materials using contact angle measurements under air and water storage over time. MATERIAL AND METHODS Nine denture relining materials were investigated in this study. Two heat-curing polymethyl-methacrylate (PMMA) denture base materials: Vertex RS, Lang, one self-curing polyethyl-methacrylate (PEMA) chairside reline resin: Rebase II, six silicone relining materials: Mucopren soft, Mucosoft, Mollosil® plus, Sofreliner Touch, GC Reline™ Ultrasoft, Silagum automix comfort were used in this experiment. Contact angles were measured using high-resolution drop shape analysis system (DSA 10-MK2, KRUESS, Germany) under three conditions (in air after setting, 1 hour water storage, and 24 hours water storage). Nine materials were classified into three groups according to material composition (Group 1: PMMA, Group 2: PEMA, Group 3: Silicone). Mean values of contact angles were compared using independent samples t-test and one-way ANOVA, followed by a Scheffe's post hoc analysis (α= 0.01). RESULTS CONTACT ANGLES OF MATERIALS TESTED AFTER AIR AND WATER STORAGE INCREASED IN THE FOLLOWING ORDER: Group 1 (PMMA), Group 2 (PEMA), Group 3 (Silicone). Heat-cured acrylic denture base resins had more wettability than silicone relining materials. Lang had the highest wettability after 24 hours of water storage. Silicone relining materials had lower wettability due to their hydrophobicity. Wettability of all denture relining materials, except Rebase II and Mollosil® plus, increased after 24 hours of water storage. CONCLUSIONS Conventional heat-cured resin showed the highest wettability, therefore, it can be suggested that heat-cured acrylic resin is material of choice for denture relining materials.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of degradation of denture base resin on bond strength to relining resins.

The purpose of this study was to evaluate the effect of degradation of a denture base resin on bond strength to relining resins. Denture base resin specimens were immersed under various conditions to simulate degradation. Tensile bond strength of denture base resin after immersion to relining resins was measured with or without surface grinding. The bond strength of denture base resin without g...

متن کامل

Time-related wettability characteristic of acrylic resin surfaces treated by glow discharge.

STATEMENT OF PROBLEM Adhesion and cohesion have important roles in denture retention, and attempts have been made to improve the wettability of the acrylic resin material by surface treatments. PURPOSE This study examined the initial and subsequent wettability of an acrylic resin denture base material treated under air or argon plasma atmosphere before and after exposure to air or distilled w...

متن کامل

A Comparative Analysis Of Retentive Qualities Of Hard Chairside Relining Materials On Maxillary Denture Base - An In Vivo Study

Corresponding author: Renu Gupta, Professor And Head, Department Of Prosthodontics, H.P.G.D.C. Shimla This article may be cited as: Gupta R, Luthra RP and Gautam D Comparative Analysis Of Retentive Qualities Of Hard Chairside Relining Materials On Maxillary Denture Base An In Vivo Study.Int J Com Health and Med Res 2017;3(2):43-48 Article Received: 11-05-17 Accepted On: 18-05-2017 NTRODUCTION T...

متن کامل

Comparative evaluation of sodium hypochlorite and microwave disinfection on dimensional stability of denture bases

PURPOSE To compare the effect of sodium hypochlorite and microwave disinfection on the dimensional stability of denture bases without and with relining. MATERIALS AND METHODS A brass die was prepared by simulating an edentulous maxillary arch. It was used to fabricate 1.5 mm and 3 mm of thickness denture bases (n = 40). The 1.5 mm of thickness-specimens (n = 20) were relined with 1.5 mm of au...

متن کامل

Histopathological examination of newly-developed adhesive silicone denture relining material

We aimed to evaluate the subcutaneous tissue reaction to a newly developed adhesive silicone denture relining material, SG, (Neo Dental Chemical Products Co., Ltd. Tokyo, Japan). We embedded the experimental material SG and another existing control material, Roeko Seal (RS), in the dorsal area of 22 male ddY mice. One week and 12 weeks after the embedding, the tissues surrounding the embedded m...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 1  شماره 

صفحات  -

تاریخ انتشار 2009