The Inhibition of Sodium Oleate for Pitting Corrosion of Aluminum Alloy 2024 in 0.1 mol L-1 NaCl Solution
نویسندگان
چکیده
The inhibition mechanism of sodium oleate (C17H33COONa) for pitting corrosion of aluminum alloy (AA) 2024 in 0.1 mol L NaCl solution was investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), scanning electron microscopy with energy dispersive spectrometer (SEM-EDS) and X-ray photoelectron spectroscopy (XPS). C17H33COONa showed good inhibition effect on uniform corrosion of AA2024 in 0.1 mol L NaCl solution by promoting surface passivity of aluminum alloy. But in NaCl solution with high concentration (3.5 wt.% NaCl), C17H33COONa could not promote passivity of aluminum alloy. C17H33COONa also suppressed the tendency of pitting initiation and reduced the pitting corrosion sensitivity of aluminum alloy. The addition of 0.1 g L C17H33COONa showed good inhibition performance but further concentration increase had little effect on the inhibition efficiency. The C17H33COO −
منابع مشابه
The Inhibition Effect of Polyethylenimine (PEI) on Pitting Corrosion of 304 Austenitic Stainless Steel in 3.5% NaCl Solution
One of the problems in the case of stainless steels is their low corrosion resistance against pitting corrosion in chloride containing environments, thereby leading to severe damage to industries. In this research, the pitting corrosion of 304 austenitic stainless steel was studied in 3.5% NaCl solution at room temperature (25˚C) by performing electrochemical measurements (containing cyclic pol...
متن کاملElectrochemical Studies of Pitting Corrosion of Cu-fe Alloy in Sodium Chloride Solutions
The electrochemical studies of pitting corrosion of CuFe alloy (70% Cu30%Fe) were carried out in sodium chloride solutions. The techniques of measurements were: open circuit potential, potentiodynamic polarization and electrochemical impedance spectroscopy. The effect of different concentrations of the inorganic additives (WO4 , PO4 , NO2 , B4O7 , CrO4 ) on the pitting corrosion of the alloy in...
متن کاملStudy of Pitting Corrosion Inhibition of Mild Steel by Nitrite in Concrete Pore Solution by Polarization and Zero Resistance Ammetery (ZRA) Techniques (RESEARCH NOTE)
A research on the corrosion inhibition of mild steel pitting corrosion in concrete pore solution by sodium nitrite was carried out by employing potentiodynamic, potentiostatic polarization and zero resistance ammetery (ZRA) techniques. Passivity breakdown potential was decreased from the transpassive potential of 700 mV at the absence of chloride to a value of -50 mV when just 0.01M NaCl was ad...
متن کاملAnti-corrosive Properties of CeO2 Conversion Coatings on Aluminum Alloy 2024 Prepared by Dip Immersion Method
As an alternative to chromate conversion coatings, rare-earth coatings especially cerium, because of the low toxicity, have attracted considerable attention. Using dip immersion method, cerium-based conversion coating was deposited on aluminum 2024. Corrosion resistance was studied in 3.5 wt.% NaCl solution using potentiodynamic polarization, electrochemical impedance spectroscopy, and surface ...
متن کاملA Galvanic Corrosion Approach to Investigating Chromate Effects on Aluminum Alloy 2024-T3
The effects of chromate treatment on the corrosion of an aluminum/copper aircraft alloy were examined with a galvanic corrosion apparatus composed of two electrodes and a zero resistance ammeter. Combinations of pure Al, pure Cu, and AA2024-T3 electrodes were immersed in 0.1 M NaCl solution, which was saturated with air, O2 , or argon. Selection of electrode material or differential aeration re...