Copper Corrosion in Aqueous Sulfide Solutions under Nuclear Waste Repository Conditions

The corrosion behavior of oxygen-free copper in anoxic sulfide solutions under nuclear waste disposal conditions was studied using electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) equipped with a focused ion beam (FIB), X-ray photoelectron spectroscopy (XPS) and Micro X-ray diffraction ( XRD). The film growth process and mechanism were elucidated using an Au marker test, and the contribution of solution diffusion to corrosion was demonstrated in magnetically-stirred experiments. The effect of groundwater chemistry, particularly chloride content on copper corrosion and film properties was characterized using long-term corrosion experiments.