Characterization of the microstructure, tensile and creep behavior of powder metallurgy processed and rolled Ti-6Al-4V-1B Alloy
نویسندگان
چکیده
This work investigated the microstructure and elevated-temperature (400-475C) tensile and tensile-creep deformation behavior of a powder metallurgy (PM) rolled Ti-6Al-4V-1B(wt.%) alloy. The PM rolled Ti-6Al-4V-1B alloy exhibited a duplex microstructure, and it did not exhibit a strong α-phase texture compared with the PM extruded Ti-6Al-4V-1B alloy. The PM rolled Ti6Al-4V-1B alloy exhibited greater creep resistance than the PM extruded Ti-6Al-4V-1B alloy as well as the as-cast Ti-6Al-4V-1B alloy.
منابع مشابه
Fabrication and characterization of the Ti-6Al-4V/Mg scaffold
Ti–6Al–4V scaffolds were fabricated by powder metallurgical space holder technique in this research. The most added magnesium (Mg) powder was evaporated and a skeleton of Ti-6Al-4V alloy was produced. For this purpose Ti-6Al-4V and Mg powders mixture compacted in a steel die by applying uniaxial pressure of 500 MPa before sintering the green product in a sealed quartz tubes at 900 °C for 2 hour...
متن کاملFatigue and corrosion fatigue properties of Ti-6Al-4V implant grade titanium alloy in Ringer solution
Nowadays modification of metallic biomaterials which are used as implants for bone and hard tissues replacement is considered as an important subject. In the current study, corrosion fatigue properties of Ti-6Al-4V alloy investigated via Rotating-Bending standard test method and then, the results compared with the fatigue properties of the specimens tested in the same conditions. Scanning elect...
متن کاملEFFECTS OF TENSILE STRENGTH ON FATIGUE BEHAVIOR AND NOTCH SENSITIVITY OF TI-6AL-4V
In this research, rotating bending fatigue test at minimum to maximum stress ratio of R=-1 was used for investigating the fatigue behavior of Ti-6Al-4V alloy. Both smooth and notched specimens, with elastic concentration factor, kt, of approximately 3.6 and 4.1 were used for this purpose.In addition, the effect of variation in ultimate tensile strength, UTS, on the fatigue behavior of this allo...
متن کاملSolid-state foaming of Ti–6Al–4V by creep or superplastic expansion of argon-filled pores
Ti–6Al–4V foams are produced by the expansion of pressurized argon pores trapped in billets created by powder metallurgy. Pore expansion during thermal cycling (840–1030 C, which induces transformation superplasticity in Ti–6Al–4V) improves both the foaming rate (by reducing the flow stress) and the final porosity (by delaying fracture of the pores and subsequent escape of the gas), as compared...
متن کاملInvestigation of the effect of temperature on the corrosion behavior of welded joints similar of titanium alloy Ti-6Al-4V by friction stir welding method
In this study, corrosion behavior of Ti-6Al-4V titanium alloy joint by friction stir welding with a rotational speed of 375 rpm and a travel speed of 100 mm/min was investigated. The welding procedure was carried out under β-transus temperature that was consisted of equiaxed grains in the stir zone. The corrosion behavior of the welded joint was investigated in 3.5% NaCl solution at temperature...
متن کامل