Fatigue Life Estimation of Medium-Carbon Steel with Different Surface Roughness
نویسندگان
چکیده
Medium-carbon steel is commonly used for the rail, wire ropes, tire cord, cold heading, forging steels, cold finished steel bars, machinable steel and so on. Its fatigue behavior analysis and fatigue life estimation play an important role in the machinery industry. In this paper, the estimation of fatigue life of medium-carbon steel with different surface roughness using established S-N and P-S-N curves is presented. To estimate the fatigue life, the effect of the average surface roughness on the fatigue life of medium-carbon steel has been investigated using 75 fatigue tests in three groups with average surface roughness (Ra): 0.4 μm, 0.8 μm, and 1.6 μm, respectively. S-N curves and P-S-N curves have been established based on the fatigue tests. The fatigue life of medium-carbon steel is then estimated based on Tanaka-Mura crack initiation life model, the crack propagation life model using Paris law, and material constants of the S-N curves. Six more fatigue tests have been conducted to validate the presented fatigue life estimation formulation. The experimental results have shown that the presented model could estimate well the mean fatigue life of medium-carbon steel with different surface roughness.
منابع مشابه
Effect of Residual Stresses on Fatigue Strength of Severely Surface Deformed Steels by Shot Peening
The compressive stress distribution below the specimen surface of severely surface deformed steels by shot peening was investigated by using laboratory X-rays and high-energy X-rays from a synchrotron radiation source, SPring-8 in the Japan Synchrotron Radiation Research Institute. Medium carbon steel plates were heat treated in two different conditions. The Vickers hardness of material-A and B...
متن کاملEffect of Aluminum on Microstructure and Thickness of Galvanized Layers on Low Carbon silicon-Free Steel
In hot dip galvanizing, several parameters such as chemical composition of coating bath, immersion time and surface roughness of specimens could affect microstructure and properties of coating. In this article, the effect of aluminum content, immersion time and surface roughness on structure and properties of alloy layers have been investigated. Specimens of low carbon silicon-free steel with d...
متن کاملLow-Carbon Steel Sheet Asymmetric Single-Point Incremental Forming: Analysis and Optimization of the Surface Roughness (TECHNICAL NOTE)
Surface roughness (SR) has an adverse effect on the appearance of low-carbon steel parts, formed in the asymmetric incremental sheet forming (AISF) process, particularly those requiring painting operation. The purpose of this study is to investigate the effects of AISF process parameters on the surface roughness of an asymmetric part formed on low-carbon steel sheets. The parameters are feed ra...
متن کاملEstimating the fatigue stress concentration factor of machined surfaces
In this study the effects of surface texture on the fatigue life of a high-strength low-alloy steel were evaluated in terms of the apparent fatigue stress concentration. An abrasive waterjet was used to machine uniaxial dogbone fatigue specimens with specific surface quality from a rolled sheet of AISI 4130 CR steel. The surface texture resulting from machining was characterized using contact p...
متن کاملAssessment of different methods for fatigue life prediction of steel in rotating bending and axial loading
Generally, fatigue failure in an element happens at the notch on a surface where the stress level rises because of the stress concentration effect. The present paper investigates the effect of a notch on the fatigue life of the HSLA100 (high strength low alloy) steel which is widely applicable in the marine industry. Tensile test was conducted on specimens and mechanical properties were obtain...