Design and Fabrication of 3D printed Scaffolds with a Mechanical Strength Comparable to Cortical Bone to Repair Large Bone Defects
نویسندگان
چکیده
A challenge in regenerating large bone defects under load is to create scaffolds with large and interconnected pores while providing a compressive strength comparable to cortical bone (100-150 MPa). Here we design a novel hexagonal architecture for a glass-ceramic scaffold to fabricate an anisotropic, highly porous three dimensional scaffolds with a compressive strength of 110 MPa. Scaffolds with hexagonal design demonstrated a high fatigue resistance (1,000,000 cycles at 1-10 MPa compressive cyclic load), failure reliability and flexural strength (30 MPa) compared with those for conventional architecture. The obtained strength is 150 times greater than values reported for polymeric and composite scaffolds and 5 times greater than reported values for ceramic and glass scaffolds at similar porosity. These scaffolds open avenues for treatment of load bearing bone defects in orthopaedic, dental and maxillofacial applications.
منابع مشابه
Mechanical performance of three-dimensional bio- nanocomposite scaffolds designed with digital light processing for biomedical applications
Introduction: The need for biocompatible and bioactive scaffolds to accelerate the regeneration and repair of fractured bones has been considered for bone tissue engineering applications during recent decades. The new methods were developed to produce scaffolds to improve the tissue quality, size of cavities, control the porosity and increase the scaffold compressive strength u...
متن کاملA Review on Commonly Used Scaffolds in Tissue Engineering for Bone Tissue Regeneration
Introduction: Bone is one of the tissues that have a true potential for regeneration. However, sometimes the bone defects are so outsized that there is no chance of bone self-repair and restoration or the damage is such that it is not possible to repair with medical or surgical interventions. In these situations, bone grafts are the treatment of choice, but due to several obstacles, including l...
متن کاملSelective Laser Sintering and Freeze Extrusion Fabrication of Scaffolds for Bone Repair Using 13-93 Bioactive Glass: a Comparison
13-93 glass is a third-generation bioactive material which accelerates the bone’s natural ability to heal by itself through bonding with surrounding tissues. It is an important requirement for synthetic scaffolds to maintain their bioactivity and mechanical strength with a porous internal architecture comparable to that of a human bone. Additive manufacturing technologies provide a better contr...
متن کاملIncreased Osteogenic Potential of Pre-Osteoblasts on Three-Dimensional Printed Scaffolds Compared to Porous Scaffolds for Bone Regeneration
Background: One of the main challenges with conventional scaffold fabrication methods is the inability to control scaffold architecture. Recently, scaffolds with controlled shape and architecture have been fabricated using 3D-printing. Herein, we aimed to determine whether the much tighter control of microstructure of 3DP PLGA/β-TCP scaffolds is more effective in promoting osteogenesis than por...
متن کاملEnhanced human bone marrow mesenchymal stem cell function on 3D printed nanobone scaffolds with microvascular network
Critical sized bone defects resulting from traumatic injury, cancer, degenerative diseases, or birth defects present a crucial clinical problem. The area of such defects is typically large and is often debilitating to those affl icted. As a multifunctional tissue comprised of both a porous nanobone extracellular matrix and an interconnected microstructure of blood vessels, it is hard to repair ...