Surface morphology in engineering applications: Influence of roughness on sliding and wear in dry fretting
نویسندگان
چکیده
Influence of initial surface roughness on friction and wear processes under fretting conditions was investigated experimentally. Rough surfaces (Ra=0.15-2.52 μm) were prepared on two materials: carbon alloy (AISI 1034) and titanium alloy (Ti-6Al-4V). Strong influence of initial surface roughness on friction and wear processes is reported for both tested materials. Lower coefficient of friction and increase in wear rate was observed for rough surfaces. Wear activation energy is increasing for smoother surfaces. Lower initial roughness of surface subjected to gross slip fretting can delay activation of wear process and reduce wear rate, however it can slightly increase the coefficient of friction.
منابع مشابه
Influence of roughness on contact interface in fretting under dry and boundary lubricated sliding regimes
This paper presents experimental results of wear process under dry and boundary lubricated metallic (AISI 1034/AISI 52100) contacting bodies with different surfaces morphologies subjected to a wide range of kinematic fretting conditions. Analysis of damage mode observed under such fretting conditions is elucidated in context of surfaces morphologies therefore associated with surface manufacturi...
متن کاملDry and Wet Wear Characteristic of TiO2 Thin Film Prepared by Magnetic Sputtering in Ringer Solution
In this research, a thin film of TiO2 was applied on AZ91D using the method of magnetic sputtering. Microstructure investigations were done using field emission scanning electron microscope (FESEM) and X-ray diffraction (XRD). Wear resistance for the coating was investigated using the pin on the disk in the form of dry and in the Ringer's solution. After this test, the worn surface of the sampl...
متن کاملStudy on tool wear and surface roughness in end milling of particulate aluminum metal matrix composite: Application of response surface methodology
Metal matrix composites have been widely used in industries, especially aerospace industries, due to their excellent engineering properties. However, it is difficult to machine them because of the hardness and abrasive nature of reinforcement elements like silicon carbide particles (SiCp).In the present study, an attempt has been made to investigate the influence of spindle speed (N), feed rate...
متن کاملTHE INFLUENCE OF DRY SLIDING ON PRCIPITATION HARDENING BEHAVIORS OF Al-Cu-Si ALLOY
Abstract: Cold working performed before an aging treatment has a significant effect on size and amount of precipitate produced. This could be caused by the increase in defect density, such as vacancies and dislocations. In this research, the Al-Cu-Si alloy was solution-treated, wear-tested and then artificially aged for a period of 1–5 h. Changes in the amount of precipitate, in the lattice par...
متن کاملMechanical Characterization and Wear Behavior of Nano TiO2 Particulates Reinforced Al7075 Alloy Composites
In the current research work synthesis, characterization, mechanical and wear behavior of 5 and 10 wt. % of nano TiO2 particulates reinforced Al7075 alloy composites are inspected. The Al7075 alloy and nano TiO2 particle composites were provided by melt stir system. After the preparation, the prepared composites were analyzed by SEM, EDS, and XRD for inquiring the microstr...
متن کامل