Large-Scale, solution-phase growth of single-crystalline SnO2 nanorods.
نویسندگان
چکیده
Small-diameter (<5 nm), single-crystalline SnO2 nanorods were synthesized in solution with a mean length of 17 +/- 4 nm (mean aspect ratio of 4:1) with the [001] direction along the major axis. Two characteristic peaks at 576 and 356 cm-1 in the Raman spectrum further confirmed the small crystal size. The SnO2 nanorods exhibit a red emission at 580 nm.
منابع مشابه
Solution-phase synthesis of single-crystalline iron phosphide nanorods/nanowires.
A solution-phase route for the preparation of single-crystalline iron phosphide nanorods and nanowires is reported. We have shown that the mixture of trioctylphosphine oxide (TOPO) and trioctylphosphine (TOP), which are commonly used as the solvents for semiconductor nanocrystal synthesis, is not entirely inert. In the current process, TOP, serving as phosphor source, reacts with Fe precursors ...
متن کاملLarge-scale electrochemical synthesis of SnO2 nanoparticles
Tin oxide nanoparticles were synthesized by electrochemical oxidation of a tin metal sheet in a nonaqueous electrolyte containing NH4F. The as-prepared nanoparticles were then thermally annealed at 700 C for 6 h. The resulting particles were characterized by a variety of experimental techniques, including X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), Raman, ...
متن کاملSynthesis of one-dimensional SnO2 nanorods via a hydrothermal technique
We have developed a simple solution process to synthesize tin oxide nanorods. The influence of precursors and the reaction temperature on the morphology of SnO2 is investigated. SnO2 nanorods are characterized by X-ray diffraction, transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Raman spectroscopy. The as-grown SnO2 nanorods are uniform in size with a radius of 5...
متن کاملGrowth of CrO [ subscript 2 ] coated single crystalline ( SnO [ subscript 2 ] ) tin oxide nanowires
Single crystalline tin oxide (SnO2) nanowires have been synthesized by carbothermal reduction of SnO2 nanopowder followed by thermal evaporation of the reduced precursor and growth via the vapor-liquid-solid (VLS) growth mechanism. The nanowires are deposited on single crystalline TiO2 substrates of orientations of (100) and (110) that are coated with a thin film and colloids of gold (Au) catal...
متن کاملMicrowave-assisted synthesis of SnO2 nanorods for oxygen gas sensing at room temperature
High-quality single-crystalline SnO₂ nanorods were synthesized using a microwave-assisted solution method. The nanorods were characterized using X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), ultraviolet-visible and Raman spectroscopy, Brunauer-Emmett-Teller (BET), and electrical resistance measurements. The XRD pattern ind...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of the American Chemical Society
دوره 126 19 شماره
صفحات -
تاریخ انتشار 2004