Fabrication and centeracterization of ordered CuIn(1−x)GaxSe2 nanopore films via template-based electrodeposition
نویسندگان
چکیده
Ordered CuIn(1-x)GaxSe2 (CIGS) nanopore films were prepared by one-step electrodeposition based on porous anodized aluminum oxide templates. The as-grown film shows a highly ordered morphology that reproduces the surface pattern of the substrate. Raman spectroscopy and X-ray diffraction pattern show that CIGS nanopore films had ideal chalcopyrite crystallization. Energy dispersive spectroscopy reveals the Cu-Se phases firstly formed in initial stage of growth. Then, indium and gallium were incorporated in the nanopore films in succession. Cu-Se phase is most likely to act as a growth promoter in the growth progress of CIGS nanopore films. Due to the high surface area and porous structure, this kind of CIGS films could have potential application in light-trapping CIGS solar cells and photoelectrochemical water splitting.
منابع مشابه
Fabrication of Graphene Oxide Thin Films on Transparent Substrate via a Low-Voltage Electrodeposion Technique
Graphene oxide (GO) thin films were simply deposited on fluorine doped tin oxide (FTO) substrate via a low-voltage electrodeposition. The GO and GO thin films were characterized by Zeta Potential, X-ray diffraction, Ultraviolet-Visible spectroscopy, atomic force microscopy, Fourier transform infrared spectroscopy, field emission scanning electron microscopy and energy dispersive X-ray spectrosc...
متن کاملFabrication of cobalt-nickel binary nanowires in a highly ordered alumina template via AC electrodeposition
Cobalt-nickel (Co-Ni) binary alloy nanowires of different compositions were co-deposited in the nanopores of highly ordered anodic aluminum oxide (AAO) templates from a single sulfate bath using alternating current (AC) electrodeposition. AC electrodeposition was accomplished without modifying or removing the barrier layer. Field emission scanning electron microscope was used to study the morph...
متن کاملFabrication and ultraviolet photoresponse characteristics of ordered SnOx (x ≈ 0.87, 1.45, 2) nanopore films
Based on the porous anodic aluminum oxide templates, ordered SnOx nanopore films (approximately 150 nm thickness) with different x (x ≈ 0.87, 1.45, 2) have been successfully fabricated by direct current magnetron sputtering and oxidizing annealing. Due to the high specific surface area, this ordered nanopore films exhibit a great improvement in recovery time compared to thin films for ultraviol...
متن کاملAluminum Nanowire Arrays via Directed Assembly.
Freestanding and vertically-oriented metal nanowire arrays have potential utility in a number of applications, but presently lack a route to fabrication. Template-based techniques, such as electrodeposition into lithographically defined nanopore arrays, have produced well-ordered nanowire arrays with a maximum pitch of about 2 μm; such nanowires, however, tend to cluster due to local attractive...
متن کاملElectrochemical fabrication of Cu/Pd multilayer nanowires in polycarbonate template
In this work,copper/palladium (Cu/Pd) multilayer nanowires were successfully prepared by electrodeposition method using polycarbonate template. The fabrication of Pd/Cu multilayer nanowires was controlled by analyzing the current–time transient during electrodeposition using potentiostat. The morphological properties of the nanowires were studied by scanning electron microscopy (SEM) and resu...
متن کامل