High-Temperature Carbon Deposition on Oxide Surfaces by CO Disproportionation

نویسندگان

  • Michaela Kogler
  • Eva-Maria Köck
  • Bernhard Klötzer
  • Thomas Schachinger
  • Wolfgang Wallisch
  • Raphael Henn
  • Christian W. Huck
  • Clivia Hejny
  • Simon Penner
چکیده

Carbon deposition due to the inverse Boudouard reaction (2CO → CO2 + C) has been studied on yttria-stabilized zirconia (YSZ), Y2O3, and ZrO2 in comparison to CH4 by a variety of different chemical, structural, and spectroscopic characterization techniques, including electrochemical impedance spectroscopy (EIS), Fourier-transform infrared (FT-IR) spectroscopy and imaging, Raman spectroscopy, and electron microscopy. Consentaneously, all experimental methods prove the formation of a more or less conducting carbon layer (depending on the used oxide) of disordered nanocrystalline graphite covering the individual grains of the respective pure oxides after treatment in flowing CO at temperatures above ∼1023 K. All measurements show that during carbon deposition, a more or less substantial surface reduction of the oxides takes place. These results, therefore, reveal that the studied pure oxides can act as efficient nonmetallic substrates for CO-induced growth of highly distorted graphitic carbon with possible important technological implications especially with respect to treatment in pure CO or CO-rich syngas mixtures. Compared to CH4, more carbon is generally deposited in CO under otherwise similar experimental conditions. Although Raman and electron microscopy measurements do not show substantial differences in the structure of the deposited carbon layers, in particular, electrochemical impedance measurements reveal major differences in the dynamic growth process of the carbon layer, eventually leading to less percolated islands and suppressed metallic conductivity in comparison to CH4-induced graphite.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Influence of electroplating parameters on microstructure and amount of ceramic particle deposition in Ni-Co-CeO2-ZrO2 composite coating

Austenitic stainless steels are high performance steels that have various applications in solid oxide fuel cells and boiler tubes under high temperature operating conditions. The Cr2O3 oxide layer formed on the steel surface becomes unstable at high temperatures and reduces the oxidation resistance of the steel. Therefore, protection of these steels at high temperatures is essential. Therefore,...

متن کامل

Characterization of Single-Walled Carbon Nanotubes (SWNTs) Produced by CO Disproportionation on Co-Mo Catalysts

The disproportionation of CO over Co-Mo/SiO2 catalysts with low Co/Mo ratios results in a high selectivity to single-walled carbon nanotubes (SWNTs) when the reaction is conducted between 700 and 950 °C in a flow of pure CO at a total pressure between 1 and 5 atm. A detailed characterization involving Raman spectroscopy, temperature-programmed oxidation (TPO), and transmission electron microsco...

متن کامل

Catalytic Oxidation of Carbon Monoxide by Cobalt Oxide Catalysts Supported on Oxidized-MWCNT

Cobalt oxide catalysts supported on oxidized multi-walled carbon nanotubes (MWCNT) for the low-temperature catalytic oxidation of carbon monoxide were prepared by an impregnation-ultrasound method. These catalysts were characterized by N2 adsorption/desorption, TEM, XRD, Raman, and H2-TPR methods. The XRD and Raman results indicated that the phase of the synthesized cobalt...

متن کامل

Gas-phase production of carbon single-walled nanotubes from carbon monoxide via the HiPco process: A parametric study

We have demonstrated large-scale production ~10 g/day! of high-purity carbon single-walled nanotubes ~SWNTs! using a gas-phase chemical-vapor-deposition process we call the HiPco process. SWNTs grow in high-pressure ~30–50 atm!, high-temperature ~900–1100 °C! flowing CO on catalytic clusters of iron. The clusters are formed in situ: Fe is added to the gas flow in the form of Fe~CO!5. Upon heati...

متن کامل

Efficient CVD Growth of Single-Walled Carbon Nanotubes on Surfaces Using Carbon Monoxide Precursor

Single Walled carbon nanotubes (SWNTs) were grown directly on flat substrates using chemical vapor deposition (CVD) method with carbon monoxide and hydrogen mixture as feeding gas. Comparing with other CVD methods, this new approach yields higher efficiency and more reproducible results in obtaining high quality SWNTs separated as individual nanotubes on substrates. Such samples can be used to ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 120  شماره 

صفحات  -

تاریخ انتشار 2016