A Study on the Aging Behavior of Al6061 Composites Reinforced with Y2O3 and TiC
نویسندگان
چکیده
Abstract: The reinforcement particles play important roles in determining microstructural development and properties of Al6061 composites. In the present work, the aging behavior of Al6061 reinforced with Y2O3 and TiC particles produced via mechanical alloying are investigated. The results indicate that the peak-aged Al6061 alloy without reinforcement demonstrates the highest hardness, which corresponds to the formation of the Mg–Si precipitates. However, precipitation formation is not observed in the case of the Al6061 composites, which can be attributed to the fact that the Mg–Si clusters and GP zones are inhibited by the presence of the reinforcement particles. The solute elements segregate in the complex oxides or carbides and contribute to only a slight increase in hardness.
منابع مشابه
Effect of Aging on Fracture Toughness of Al6061-Graphite Particulate Composites
This article presents the investigative work conducted on the fracture toughness and microstructure of Al6061-9% graphite particulate composites. The requisite specimens for the fracture toughness testing were compact tension ones prepared using stir casting technique. The Al6061-9% graphite particulate metal matrix composite has been heat treated in the underaged condition. It is observed from...
متن کاملTribological Behavior of Reinforced and Unreinforced High Chromium Cast Iron
In this paper, the metal matrix composites containing 22 wt % Cr, 2.5 wt % C and 2 to 16 volume percent TiC were processed by solidifying Fe-Cr-Ti-C in which precipitation of titaniumcarbide and chromium carbide occurred. The microstructure and abrasion resistance of in-situ synthesized composites were compared with the unreinforced high chromium white cast iron (HCWCI) containing 22 w. t. % C...
متن کاملThe Effect of TiC Additive with Al2O3-Y2O3 on the Microstructure and Mechanical Properties of SiC Matrix Composites
In this research, the SiC-matrix composite with different amounts of TiC (0, 2.5, 5, 7.5, and 10 wt%) supplemented with additives including 4.3 wt% Al2O3 and 5.7 wt% Y2O3 were utilized to initiate the required liquid phase. The sintering process was performed using pressureless sintering at 1900 °C for 1.5 hours under argon atmosphere. The compos...
متن کاملAccelerated Heat Aging Study of Phenolic/Basalt Fiber Reinforced Composites
One of the greatest impediments to use polymer-matrix composites is their susceptibility to degradation when exposed to the elevated temperatures and the limited knowledge on the thermal and mechanical properties of these composites at such temperatures. The objective of this study is to evaluate the effects of accelerated heat aging on the tensile properties of the Woven Basalt/Phenolic (WBP) ...
متن کاملبررسی تأثیر فرآیند اکستروژن بر ریزساختار و استحکام کامپوزیت Al6061-SiC
Al-SiC composites are among the most demanding metal matrix composites due to their excellent strength, good ductility, good corrosion resistance, low coefficient of thermal expansion and reasonable price. Manufacturing of cast metal matrix composites usually involves some problems such as inhomogeneous distribution of the particles due to poor wetability of ceramics to molten alloys, porosity ...