High capacitance of surface-modified 2D titanium carbide in acidic electrolyte
نویسندگان
چکیده
منابع مشابه
EDLC performance of carbide-derived carbons in aprotic and acidic electrolytes
This study shows that carbide-derived carbons (CDCs) with average pore size distributions around 0.9 to 1 nm and effective surface areas of 1300-1400 m g provide electrochemical double layer capacitors with high performances in both aqueous (2M H2SO4) and aprotic (1M (C2H5)4NBF4) in acetonitrile) electrolytes. In the acidic electrolytic solution, the gravimetric capacitance at low current densi...
متن کاملTitanium Carbide Derived Nanoporous Carbon for Energy-Related Applications
High surface area nanoporous carbon has been prepared by thermo-chemical etching of titanium carbide TiC in chlorine in the temperature range 200–1200 °C. Structural analysis showed that this carbide-derived carbon (CDC) was highly disordered at all synthesis temperatures. Higher temperature resulted in increasing ordering and formation of bent graphene sheets or thin graphitic ribbons. Soft X-...
متن کاملSynthesis of Titanium Carbide by the Combustion of TiO2-2Mg-C and 3TiO2-4Al-3C Systems in a Tubular Furnace
The combustion process of TiO2- 2Mg- C and 3TiO2-4Al-3C systems in a tubular furnace was investigated. TiC has been synthesized by the magnesiothermic reaction from a mixture of compacted powders of TiO2, Mg and charcoal as starting materials in the presence and absence of NaCl. The effects of temperature, pressure, and the stoichiometry ratio in the reactio...
متن کاملProbing the Mechanism of High Capacitance in 2D Titanium Carbide Using In Situ XRay Absorption Spectroscopy
(comparable only with hydrated RuO 2 ) was measured for Ti 3 C 2 T x in aqueous electrolytes. [ 11,14 ] Our previous studies revealed that spontaneous intercalation of some cations takes place when MXene samples are exposed to aqueous electrolytes. [ 6 ] In situ X-ray diffraction showed that variations of the distance between the Ti 3 C 2 T x layers (which is proportional to the c lattice param...
متن کاملSupercapacitive Performance of Ordered Mesoporous Carbon (CMK-3) in Neutral Aqueous Electrolyte
Ordered Mesoporous Carbon (OMC) represents an interesting material for electric double layer capacitors which has the high surface area, easily accessed ordered pore channels and lower production cost. In this work, CMK-3 as promising OMC has been fabricated using the ordered mesoporous silica SBA-15 as a template. The structure and morphology of CMK-3 are characterized by X-ray diffraction...