The effect of coloring liquid dipping time on the fracture load and color of zirconia ceramics
نویسنده
چکیده
PURPOSE The aims of the study were to evaluate the fracture load of zirconia core material after dipping in coloring liquid at different time intervals and to compare the color of dipped blocks with that of prefabricated shaded blocks. MATERIALS AND METHODS 3-unit bridge frameworks were designed digitally. Sixty frameworks were fabricated using uncolored zirconia blocks by CAD/CAM and divided into 4 groups randomly (n = 15). Group 2 (G2) was subjected to coloring liquids for 2 minutes, Group 4 (G4) for 4 minutes, and Group 6 (G6) for 6 minutes. CFS group was not subjected to any coloring procedure. After coloring, color differences between the test groups and a prefabricated shaded zirconia group (CPZ, n = 15) were evaluated by using a spectrophotometer. Fracture test was conducted immediately after shade evaluation with a Testometric test device at a cross-head speed of 1 mm/sec. Statistical analysis for evaluating color and fracture load was performed by using one way ANOVA followed by Tukey HSD test (P ≤ .05). Weibull analysis was conducted for distribution of fracture load. RESULTS There was no difference in terms of fracture load and color between CFS (1176.681 N) and G2 (985.638 N) group and between CPZ (81.340) and G2 (81.140) group, respectively. Fracture load values of G4 (779.340 N) and G6 (935.491 N) groups were statistically significantly lower than that of CFS group (P ≤ .005). The color values of G4 (79.340) and G6 (79.673) groups were statistically different than that of CPZ group (P ≤ .005). CONCLUSION Prolonged immersion of zirconia in coloring liquid not only negatively affected the fracture load of the zirconia being tested in the current study but also deteriorated the desired shade of the restoration.
منابع مشابه
The effect of different surface treatment methods on the color stability of monolithic zirconia
Abstract Background & aim: There are so many studies about effect of colored drinks and mouthwashes on discoloration of different dental ceramics. However, little is known regarding the effect of colored drinks on discoloration of monolithic zirconia .The purpose of this invitro study was to evaluate the effect of different surface treament methods on color stability of monolithic zirconia....
متن کاملThe Effect of Different Solutions on Optical Behavior of Polished and Glazed Zirconia-Reinforced Lithium Silicate Ceramics
Background: This study sought to assess the effect of glazing and polishing surface treatments on the optical behavior of zirconia-reinforced lithium silicate ceramics thermocycled in different solutions. Methods:Computer-aided design/computer-aided manufacturing ceramics (VITA Suprinity) were cut into samples (n=104) measuring 1.5x14x10 mm according to t...
متن کاملComparison of the effect of chlorhexidine and listerine on the stability of the monolithic glazed zirconium dye and the IPS-e.max glazed ceramics( in vitro)
Abstract Background and aim: Regarding the prevalence of monolithic zirconia and glazed ceramics IPS-e.max, and inadequate research on the color change of chlorhexidine and listerine mouthwashes on these two types, this study was aimed to compare the effect of these two mouthwashes on the stability of the The mentioned materials. Materials and Methods: This experimental study was carried o...
متن کاملIn Vitro Effect of Zirconia and Zirconia Enriched Glass Fiber Composite Posts on Fracture Resistance of Endodontically Treated Teeth
Objective: Despite the advantages of esthetic posts, lack of studies on their fracture resistance has limited their clinical use. This study aimed to compare the effect of two types of esthetic posts namely zirconia and zirconia enriched glass fiber composite posts on fracture resistance of endodontically treated teeth against compressive forces. Methods: This in vitro study was conducted o...
متن کاملEffect of the amount of thickness reduction on color and translucency of dental monolithic zirconia ceramics
PURPOSE This study investigated the effect of amount of thickness reduction on color and translucency of dental monolithic zirconia ceramics. MATERIALS AND METHODS One-hundred sixty-five monolithic zirconia specimens (16.3 mm × 16.3 mm × 2.0 mm) were divided into 5 groups (Group I to V) according to the number of A2-coloring liquid applications. Each group was then divided into 11 subgroups b...
متن کامل