Hot Ductility Loss in a Fe-Ni-Based Superalloy
نویسندگان
چکیده
High temperature tensile tests have been conducted on samples of a Fe-Ni based superalloy, Incoloy A-286, and significant ductility loss has been observed at 1220 °C. Titanium-rich, thin-film-like phase has been found on the inter-granular facets of fracture surfaces. It appears that sulfur content of Ti-rich phase was higher than that of the matrix. At 1220 °C, liquation of Ti-rich phases has resulted in thin-film-like morphology along the grain boundary and caused the ductility loss during tensile deformation.
منابع مشابه
Study of a New Type High Strength Ni-Based Superalloy DZ468 with Good Hot Corrosion Resistance
متن کامل
Determination of solution temperature in an ex-service Ni-based turbine blade
It is well-known that the harsh operational conditions of turbine blades lead to a gradual change in the microstructure of underlying Ni-based superalloy of blades. According to this, a rejuvenation process should be conducted on turbine blades superalloys to recover their microstructures. The first and main step of rejuvenation process is the determination of appropriate solution condition in ...
متن کاملEvaluating the Effect of Ta/W Ratio on Microstructure and Stress Rupture Properties of Ni-Based Single Crystal Superalloy PWA1483
In this study, the effect of Ta/W ratio on the microstructure and stress rupture properties of Ni-based single crystal (SX) superalloy PWA1483 was investigated. For this purpose, single crystal (SX) superalloys with different Ta/W ratios (0.75, 1.0, 1.32 and 1.5 in wt.%) were fabricated. The alloys were directionally solidified by Bridgman method under the same solidification condition at withd...
متن کاملFinal report: Aluminium based Nanoeutectics: Synthesis and Microstructure
Abstract: The primary aim of the project was to explore the possibility of synthesising high strength multiphase eutectic alloys based on aluminium which also exhibits reasonable ductility. The approach used was to develop a multiscale microstructure including nanometer length scale eutectic colony using ternary alloys and evaluate their deformation behaviour. We have carried out work on two al...
متن کاملNickel-based Superalloy Layer Deposited on AISI H13 Hot Tool Steel Base Metal Using Explosion Cladding process
An experimental test was carried out to explosively clad solution annealed Inconel 718 superalloy on quench-tempered AISI H13 hot tool steel. A wavy with vortices interface geometry was obtained from this experiment. A gradual change in the wavelength along the direction of welding was observed which was due to a change in the impact angle, following the plate contacts. In this paper, the exper...
متن کامل