Effect of polyethylene pretreatments on the biomimetic deposition and adhesion of calcium phosphate films.
نویسندگان
چکیده
The effect of ultraviolet irradiation and glow discharge (GD) processing of the polyethylene (PE) substrates on deposition of calcium phosphate (CaP) films from supersaturated aqueous calcium phosphate solutions was investigated in this study. CaP coatings deposited on the PE substrates were comprised of elongated clusters of spherical particles and 100% of the free surface area of nearly all of the substrates was covered with a porous CaP film after a 3 day immersion. Nano-scratch tests determined that PE-CaP adhesion was most improved when PE substrates were subjected to 50W GD treatments. As determined by contact angle measurements, the GD-treated PE samples had the highest electron donor parameter of surface energy, suggesting that enhancing the electron donor parameter of PE leads to improved adhesion with the biomimetic CaP coating.
منابع مشابه
Effect of Alkaline-Acid Treatment on the Biomimetic Formation of Calcium Phosphate Layers on Titanium Substrates:An In Vitro Study
متن کامل
Surface Activation of NiTi Alloy by Using Electrochemical Process for Biomimetic Deposition of Hydroxyapatite Coating (TECHNICAL NOTE)
Electrochemical depositions of calcium phosphate (Ca-P) film on NiTi alloy in concentrated simulated body flood (SBF×5) were carried out by cathodic polarization. The Ca-P layer was successfully deposited on Ni-Ti alloy substrate under 10mA/cm2 current density for 2 hours at room temperature. Then, in order to investigate the bioactivity of the pre-calcified samples, they were immersed in SBF f...
متن کاملCharacterization of Biomimetic Calcium Phosphate Deposited on Chitosan for Orthopedic Implant Applications
+Chesnutt, BC; +Yuan YL; *Yang Y; *Ong JL; +Haggard WO; +Bumgardner JD Joint Program in Biomedical Engineering,+University of Memphis and *University of Tennessee-Memphis, Memphis, TN; [email protected] Introduction Chitosan is a deacetylated form of chitin, a natural polysaccharide found mainly in the exoskeletons of crustaceans. Chitosan is an attractive biomaterial because it is very biocom...
متن کاملThe effects of inorganic additives to calcium phosphate on in vitro behavior of osteoblasts and osteoclasts.
This study describes a medium-throughput system based on deposition of calcium phosphate films in multi-well tissue culture plates that can be used to study the effect of inorganic additives on the behavior of osteoblasts and osteoclasts in a standardized manner. All tested elements, copper, zinc, strontium, fluoride and carbonate were homogenously deposited into calcium phosphate films in vary...
متن کاملEffect of Alkali and Heat Treatment on Biomimetic HA Coating on Ti6Al4V
In this study, time of calcium phosphate formation on Ti6Al4V alloy with or without alkali and heat treatments was investigated. Specimens were soaked in 0, 5, 10 M solutions of NaOH at temperatures of 60 or 80 °C for 24, 72 h. Their surfaces were characterized using scanning electron microscopy and thin film X-ray diffraction. It was found that optimum condition is 72h soaking in 5 M NaOH in 8...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Acta biomaterialia
دوره 3 3 شماره
صفحات -
تاریخ انتشار 2007