Effects of H20 on structure of acid-catalysed SiO 2 sol-gel films
نویسندگان
چکیده
Thin silica films were deposited on silicon wafers by the sol-gel technique, using spin coating. The sols were prepared by HC1 catalysis of tetraethylorthosilicate (TEOS) diluted in ethanol, using different molar ratios, R, of H20:TEOS. The films were then baked at various temperatures, and characterised using ellipsometry, profilometry, optical scattering and infrared spectroscopy. It was found that the thickness, shrinkage, porosity and pore sizes all decrease with increasing R. It was also found that high water levels yield films of higher homogeneity and finer texture, and less tensile stress.
منابع مشابه
Preparation and Characterization of WO3 Electrochromic Films Obtained by the Sol-Gel Process
Tungsten trioxide (WO3) films have been coated on indium thin oxide (ITO) conductive glass substrate, using aqueous solution of peroxotungstic acid (PTA) by the sol-gel dip coating method. X-ray diffractometery (XRD) analysis confirmed monoclinic and triclinic structure for the film and powdered WO3 respectively. Fourier transforms infrared spectroscopy (FT-IR) exhibit...
متن کاملSol-gel spin coating derived ZnO thin film to sense the acetic acid vapor
ZnO thin film of 80 nm thickness was deposited by the sol-gel spin coating method on SiO2/Si substrate and subsequently post-annealed at 500°C with a flow of oxygen for 60 min. Crystallographic structure of the sample was characterized by X-ray diffraction (XRD) method while a field emission scanning electron microscope (FESEM) was used to investigate the surface physical morphology ...
متن کاملSol-gel spin coating derived ZnO thin film to sense the acetic acid vapor
ZnO thin film of 80 nm thickness was deposited by the sol-gel spin coating method on SiO2/Si substrate and subsequently post-annealed at 500°C with a flow of oxygen for 60 min. Crystallographic structure of the sample was characterized by X-ray diffraction (XRD) method while a field emission scanning electron microscope (FESEM) was used to investigate the surface physical morphology ...
متن کاملSynthesis of Unsymmetrical Ethers Catalysed by Polyvinyl Sulfuric Acid & PVSA / Nano RH SiO2 as a Novel Solid Acid Nanocomposite
The methodology involves preparing polyvinyl sulfuric acid as a solid acid by simple mixing ofpolyvinyl alcohol with chlorosulfonic acid in CH2Cl2 at room temperature. The catalytic ability ofthe solid acid was investigated for the facile conversion of benzylic alcohols to the unsymmetricalethers with aliphatic alcohols in the presence of the solid acid. Results show that the solid acid isan ap...
متن کاملEffects of UV irradiation treated polycarbonate substrates on properties of nanocrystalline TiO2 sol-gel derived thin films
In this study, in order to achieve effective coating of the homogeneous titanium dioxide (TiO2) thin film, UV irradiation pre-treatment was carried out to activate PC surfaces before coating. Sol-gel-based nanocrystalline TiO2 thin films were prepared by employing tetrabutyl-titanate as a precursor. Nanocrystalline TiO2 thin films were deposited by sol-gel spin coating on the treated substrates...