Crystal Growth and Luminescence Properties of Dy3+ and Ge4+ Co-Doped Bi4Si3O12 Single Crystals for High Power Warm White LED

نویسندگان

  • Tian Tian
  • Haiwei Feng
  • Yan Zhang
  • Ding Zhou
  • Hui Shen
  • Hongchao Wang
  • Jiayue Xu
  • Ingo Hartenbach
چکیده

Φ1 inch Dy3+ and Ge4+ co-doped bismuth silicate (Bi4Si3O12, BSO) single crystals with the length of 80–100 mm were successfully grown by Bridgman method. They are transparent, free of cracks and inclusions. The white residual at the top parts of BSO crystals disappears with co-doping 1 mol% Dy3+ and more than 3 mol% Ge4+. The FWHM values of X-ray rocking curves shows 1%Dy,3%Ge:BSO crystal possesses high crystallization quality. The intrinsic emission peak of BSO and the characteristic emission peaks of Dy3+ ions are weakened with increasing the doping concentration of Ge4+. 1 mol% Dy3+ and 3 mol% Ge4+ are the optimal concentrations due to high crystallization quality and moderate emission intensity. The CIE coordinates and CCT values shift towards warmer white light region with increased Ge4+ co-doping. The CCT values are close to the ideal value of 3000 K for warm white light when 1%Dy,3%Ge:BSO crystal is excited by various UV light. Increasing the temperature from 298 K to 573 K leads the luminescence lifetime to decrease from 659 μs to 645 μs. More than 95% and 80% photoluminescence intensity at room temperature is still retained at 423 K and 573 K respectively. Dy,Ge:BSO crystals are potential candidates for fabricating high power warm WLEDs.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Luminescence and scintillation characterization of Silver doped KCl single crystal grown by Czochralski technique for photonic applications

In this study, the scintillation and optical properties of pure and silver doped potassium chloride (KCl:Ag) single crystals were reported. Pure and doped KCl bulk single crystals with a good optical quality and free from cracks were grown from the melt using Czochralski technique. Different analysis methods were used to study the optical and scintillation properties of the grown crystals. The ...

متن کامل

Growth of CsI(Tl) crystals doped with Ca and Tm and investigation of its scintillation characteristics

In this work, the growth of CsI(Tl) crystals as gamma detector was performed using vertical Bridgman method with Ca and Tm co-dopants. For evaluation of the growth crystals, X-Ray Diffraction (XRD), photoluminescence and thermoluminescence spectra as well as recorded gamma spectra were employed. In addition, the scintillation properties including energy resolution, scintillation decay time, abs...

متن کامل

Eu3+-doped Bi4Si3O12 red phosphor for solid state lighting: microwave synthesis, characterization, photoluminescence properties and thermal quenching mechanisms

Europium-doped bismuth silicate (Bi4Si3O12) phosphor has been prepared by microwave irradiation method and its crystal structure is determined using Rietveld method. As-prepared phosphor consists of spherical, monodispersed particles with few agglomeration, high crystallinity, and narrow grain size distribution. The phosphor can be efficiently excited in the wavelength range of 260-400 nm, whic...

متن کامل

Detection of Polymer Brushes developed via Single Crystal Growth

Single crystals consisting various surface morphologies and epitaxial structures were applied to investigate the effect of other phase regions in the vicinity of a given tethered chains-covered area having a certain molecular weight of amorphous brushes. The designed experiments demonstrated that regardless of the type of surface morphology (patterned and especial mixed-brushes, homo and co...

متن کامل

Luminescence properties and warm white LED application of a ternary-alkaline fluoride red phosphor K2NaAlF6:Mn4+ .

Herein, a Mn4+ ion doped complex ternary-alkaline fluoride red phosphor K2NaAlF6:Mn4+ has been synthesized through a facile two-step co-precipitation method at room temperature. The crystal structure, morphological properties and influence of the dopant concentration, temperature and humidity on luminescence properties as well as the performance of the as-synthesized phosphor used in white ligh...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2017