Percolation transition in the porous structure of latex-templated silica monoliths
نویسندگان
چکیده
Porous sol-gel silica monoliths are prepared using PMMA nanoparticles, 60 nm in diameter, as sacrificial templates. The pore-structure of the calcined pellets is investigated through nitrogen adsorption to assess the evolution of the porosity when varying the amount of porogen. The latex templated monoliths present a well defined spherical extrinsic porosity and an intrinsic microporosity due to preparation process. As a result of a careful analysis of the adsorption hysteresis, we identify a percolation threshold of the spherical porosity around 30% volume fraction. This phenomenon, similar
منابع مشابه
Silica monoliths templated on L3 liquid crystal.
Dimensionally stable, optically clear, highly porous (approximately 65% of the apparent volume), and high surface area (up to 1400 m(2)/g) silica monoliths were fabricated as thick disks (0.5 cm) by templating the isotropic liquid crystalline L(3) phase with silica through the hydrolysis and condensation of a silicon alkoxide and then removing the organic constituents by supercritical ethanol e...
متن کاملInvestigating the Effect of Ultrasonification Time on Transition from Monolithic Porous Network to Size-Tunable Monodispersed Silica Nanospheres via Stöber Method
Abstract Uniform colloidal monodispersed silica nanoparticles were synthesized via stöber method using ammonia as a basic catalyst. Field Emission Scanning Electron Microscope (FESEM) was confirmed the homogeneous nanospheres. The decrease of TEOS concentration (0.067 to 0.012 mol L-1) and an increase of H2O concentration (3 to 14 mol L-1) at 14 mol L-1 NH3 fixed accelerated the rate of h...
متن کاملFormation of bimodal porous silica-titania monoliths by sol-gel route
Silica-titania monoliths with micrometer-scale macroporous and nanometer-scale mesoporous structure and high titania contents are prepared by sol-gel process and phase separation. Titanium alkoxide precursor was not effective in the preparation of high titania content composites because of strong decrease in phase separation tendency. Bimodal porous gels with high titania content were obtained ...
متن کاملSynthesis of emulsion-templated porous polyacrylonitrile and its pyrolysis to porous carbon monoliths
PolyHIPEs are emulsion-templated polymers synthesized within high internal phase emulsions (HIPEs). The miscibility of acrylonitrile (AN) with water has made it difficult to synthesize PAN-based polyHIPEs. This paper describes the successful synthesis of PAN-based polyHIPEs by crosslinking through copolymerization with divinylbenzene (DVB), by stabilization with a polyglycerol polyricinoleate s...
متن کاملPreparation and SPE Applications of Silica-Based Monoliths
The monolithic column is a single piece of a continuous rigid porous polymer that possesses an interconnected skeletal structure and contains pores. According to their components, monolithic materials can be divided into organic polymer-based monoliths and inorganic silica-based monoliths. This review focuses on silica-based monolith with special emphasis on the preparation. Moreover, this revi...