Interfacial microscopic examination and chemical analysis of resin - dentin interface of self - adhering flowable resin composite

نویسنده

  • Nadia A. Badr
چکیده

The newly introduced self-adhering flowable resin-composites Background: decrease the required time for application by incorporation of an acidic adhesive monomer, thus reducing the number of the steps, but its bonding is still uncertain. The aim of this study was to evaluate the interfacial microscopic examination and chemical analysis at the resin-dentin interface of a self-adhering flowable resin composite (Vertise-Flow) versus a total-etch (Te-Econom Plus) resin composite, using an etching agent (Eco-Etch gel) and bonding agent (Single Bond Universal). Sixteen freshly extracted sound human posterior teeth were used. Methods: The teeth were randomly divided into two groups: 8 specimens per type of composite. Standard-shaped class V cavities were prepared on the buccal surface. One group was restored by Te-Econom Plus resin composite by total-etch technique using Eco-Etch gel, which was applied to dentine for 15 seconds, followed by rinsing, drying and bonding agent application (Single Bond Universal). The other group restored directly with self-adhering resin composite (Vertise-Flow) without application of etch or bond. Curing was done for 20 seconds using a light emitting diode light curing unit. Evaluation of the resin-dentin interface was done microscopically by examination of marginal gap distance in μm using scanning electron microscope (SEM), and chemical analysis of silver particles was observed using SEM with energy-dispersive X-ray spectrometry after 24 hours of specimen storage in ammoniacal silver nitrate. Regarding marginal gap distance (μm) and silver atomic % mean Results: values, teeth restored with self-adhering resin composite (Vertise-Flow) showed significantly higher mean values than the multi-step etch and rinse resin composite group (5.2 0; 12.2 8.2, respectively). vs vs Resin-dentin bonding using total-etch resin composite technique Conclusions: was more effective than self-adhering flowable resin composite (Vertise-Flow) regarding marginal gap formation and penetration of silver particles. Further studies for bond strength could be performed. 1

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Interfacial microscopic examination and chemical analysis of resin-dentin interface of self-adhering flowable resin

The newly introduced self-adhering flowable resin-composites Background: decrease the required time for application by incorporation of an acidic adhesive monomer, thus reducing the number of steps, but its bonding is still uncertain. The aim of this study was to evaluate the interfacial microscopic examination and chemical analysis at the resin-dentin interface of a self-adhering flowable resi...

متن کامل

Interfacial microscopic examination and chemical analysis of resin-dentin interface of self-adhering flowable resin composite

Background: The newly introduced self-adhering flowable resin-composites decrease the required time for application by incorporation of an acidic adhesive monomer, thus reducing the number of steps, but its bonding is still uncertain. The aim of this study was to evaluate the interfacial microscopic examination and chemical analysis at the resin-dentin interface of a self-adhering flowable resi...

متن کامل

The Effect of Energy Densities on the Shear Bond Strength of Self-Adhering Flowable Composite to Er:YAG Pretreated Dentin

Objective. To investigate the shear bond strength of self-adhering flowable resin composite, to dentin, after exposing it to Er:YAG laser radiation, at different energy densities. Materials and Methods. Sixty freshly extracted human third molars were randomly divided into five groups (n = 12). In the control group, dentin was left unirradiated, whereas, in the other four groups, dentin was irra...

متن کامل

Marginal gap repair with flowable resin-based composites.

This study was designed to test the hypothesis that the flowable/dentin interface has the weakest bond and highest frequency of failure when a resin-based composite is repaired using a flowable composite. Comparing three specific groups--dentin, flowable composite, and hybrid composite-under the Kruskal-Wallis test showed that the mean bond strength values at the flowable/dentin interface and w...

متن کامل

Scanning Electron Microscopic Evaluation of Composite Resin-Dentin, Calcium Hydroxide-Dentin and Resin- Calcium Hydroxide Interfacial Gap with Composite Resin Restorations- An in vitro Study

The dental pulp has been shown to have its own reparative capacity and is capable not only of healing but also of providing a dentinal bridge in the absence of calcium hydroxide. The present study was performed to evaluate interfacial gaps formed due to polymerization shrinkage of composite resin. 20 Maxillary or Mandibular, freshly extracted human third molars were prepared and filled using co...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2017