Structure, nonlinear properties, and photosensitivity of (GeSe2)100-x(Sb2Se3)x glasses
نویسندگان
چکیده
Chalcogenide glasses from (GeSe2)100-x(Sb2Se3)x system were synthesized, with x varying from 5 to 70, in order to evaluate the influence of antimony selenide addition on nonlinear optical properties and photosensitivity. Nonlinear refractive index and two photon absorption coefficients were measured both at 1064 nm in picosecond regime using the Z-scan technique and at 1.55 μm in femtosecond regime using an original method based on direct analysis of beam profile change while propagating in the chalcogenide glasses. The study of their photosensitivity at 1.55 m revealed highly glass composition dependent behavior and quasi-photostable compositions have been identified in femtosecond regime. To better understand these characteristics, the evolution of the glass transition temperature, density and structure with the chemical composition were determined. © 2014 Optical Society of America OCIS codes: (160.2750) Glass and other amorphous materials; (160.4760) Optical properties; (190.4400) Nonlinear optics, materials; (300.6450) Spectroscopy, Raman.
منابع مشابه
Structural Investigation, Physical and Optical Properties of Mixed Alkali Bismuth Borate Glasses
Lead free, eco-friendly bismuth borate glasses doped with alkali oxides of composition xLi2O+(30-x)Na2O+55B2O3+15Bi2O3 (x = 5,10,15,20,25) were prepared by melt quenching technique. Amorphous nature of glasses was confirmed by X-ray diffraction. Density measurements were carried out at room temperature by standard principle of Archimedes with Xylene as an immersion liquid. The non-linear ...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملMicrostructure, mechanical and thermal properties of chalcogenide glasses and glass-ceramics based on Se-As-Ge system nucleated by Sn
In particular, chalcogenide glasses and glass-ceramics are new materials that exhibit good transparency in infrared region (0.8-12µm). We can overcome the main weakness of these glasses by improving the hardness through controlling crystallization. In this paper, we report results of a study on chalcogenide glasses in the ternary system of As-Se-Ge with nominal composition of Snx (Se...
متن کاملFabrication and Structural Characterization of Se-Ge Chalcogenide Glasses by Means of Melt Quenching Technique
The structural and optical characterization of Se-Ge alloys during melt quenching technique was the goal of this study. In this regards, five different samples of Se100-xGex (x= 10, 20, 30, 40, 50) were prepared by conventional melt quenching in quartz ampoule. The produced samples were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calori...
متن کاملThe Relationship between Structural and Optical Properties of GeO2-PbO Glasses
The structural and optical characterization of bulk GeO2-PbO glasses was the goal of this study. In this regard, six different (100-x)GeO2-xPbO (15<x<45) glasses were prepared by conventional melt quenching technique between two steel sheets. The produced samples were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared (FTIR) and UV-Vis s...
متن کامل