Bimetallic non-alloyed NPs for improving the broadband optical absorption of thin amorphous silicon substrates
نویسندگان
چکیده
We propose the use of bimetallic non-alloyed nanoparticles (BNNPs) to improve the broadband optical absorption of thin amorphous silicon substrates. Isolated bimetallic NPs with uniform size distribution on glass and silicon are obtained by depositing a 10-nm Au film and annealing it at 600°C; this is followed by an 8-nm Ag film annealed at 400°C. We experimentally demonstrate that the deposition of gold (Au)-silver (Ag) bimetallic non-alloyed NPs (BNNPs) on a thin amorphous silicon (a-Si) film increases the film's average absorption and forward scattering over a broad spectrum, thus significantly reducing its total reflection performance. Experimental results show that Au-Ag BNNPs fabricated on a glass substrate exhibit resonant peaks at 437 and 540 nm and a 14-fold increase in average forward scattering over the wavelength range of 300 to 1,100 nm in comparison with bare glass. When deposited on a 100-nm-thin a-Si film, Au-Ag BNNPs increase the average absorption and forward scattering by 19.6% and 95.9% compared to those values for Au NPs on thin a-Si and plain a-Si without MNPs, respectively, over the 300- to 1,100-nm range.
منابع مشابه
The effect of temperature on optical absorption cross section of bimetallic core-shell nano particles
In this paper, the temperature dependence on optical absorption cross section of the core shell bimetallic nanoparticles (NPs) is investigated in quasi static approximation. Temperature dependence of the plasmon resonance is important issue because of recent applications of NPs of noble metal for heat treating of cancer and the computer chips. The effect of temperature on surface plasmon resona...
متن کاملOptical properties of silicon nano layers by using Kramers- Kronig method
Silicon thin layers are deposited on glass substrates with the thickness of 103 nm, 147 nm and 197 nm. The layers are produced with electron gun evaporation method under ultra-high vacuum condition. The optical Reectance and the Transmittance of produced layers were measured by using spectrophotometer. The optical functions such as, real and imaginary part of refractive index, real and imaginar...
متن کاملPreparation and Characterization of Aluminum Nitride Thin Films with the Potential Application in Electro-Acoustic Devices
In this work, aluminum nitride (AlN) thin films with different thicknesses were deposited on quartz and silicon substrates using single ion beam sputtering technique. The physical and chemical properties of prepared films were investigated by different characterization technique. X-ray diffraction (XRD) spectra revealed that all of the deposited films have an amorphous str...
متن کاملPhonon-coupling enhanced absorption of alloyed amorphous silicon for solar photovoltaics
Using the observed temperature dependence of a-Si:H photon absorption spectrum and the weak-phonon interaction second-order transition theory, phonon-coupling enhanced photon absorption is predicted for a-Si-Ge and a-Si-Sn alloys. The ab initio calculated electron and phonon properties of the alloyed amorphous phase show minimally altered electronic states and significant redshifted phonon ener...
متن کاملOptoelectronic Properties of Amorphous Silicon the Role of Hydrogen: From Experiment to Modeling
Amorphous silicon, and its more useful alloy form, hydrogenated amorphous silicon (a-Si:H), has been the subject of investigation for more than three decades. A-Si:H is a lowcost, efficient material which is used extensively for electronic devices. Indeed, most recent electronic device textbooks contain a comprehensive review of the physics of amorphous materials and amorphous silicon in partic...
متن کامل