Effect of Welding Parameters on Hot Cracking Susceptibility
نویسنده
چکیده
The varestraint cracking test was carried out to assess the hot cracking tendency of alloy 800 at different welding conditions and augmented strain levels. The test results revealed that the hot cracking susceptibility of alloy 800 increases with increasing the heat input and augmented strain levels. This emphasizes the role of constraint either internally induced or externally applied to the welded structure. A cracking threshold or the minimum augmented strain (• ̧min) below which no hot cracking takes place has been found to be 0.25 for alloy 800. Also, the Critical Strain Rate to Time (CSS) required to cause cracking was found to be 6.42•~10•¬-3 sec•¬-1 at welding condition of 100 Amp, 13 Volt and 140 mm/min.
منابع مشابه
Effect of Nonmetallic Inclusions on Steel Welds Metal Hot Cracking
B. Z orc, W elding I nstitute, L jubljana, S lovenia; M . I mamović, Un iversity of Zenica, Faculty of Mechanical Engineering, Zenica, B a nd H; A. Nagode, B. Kosec, L. Kosec, University of Ljubljana, Faculty of Natural Sciences and Engineering, Ljubljana, Slovenia; A. Stoić, I. Samardžić, University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia Intercrystally distributed n...
متن کاملHot cracking in tungsten inert gas welding of magnesium alloy AZ91D
Plates of 3–5 mm in thickness were extracted from an AZ91D ingot and then butt joints of the plates were produced using tungsten inert gas (TIG) welding method. The TIG arc was also used to deposit welding beads on some of the thin plates. No cracking was found in the butt joints. However, hot cracking was always observed to propagate from the heat affected zone (HAZ) under the welding bead int...
متن کاملEffect of Heat Input on Microstructure and Mechanical Properties in Friction Stir Welding of HSLA-60
High-strength low alloy steels are a class of steels used in applications that require high strength and good weldability, including ship hulls, gas pipelines and oil industry. One way to build parts is fusion welding that create areas with a large grain size in the heat-affected zone and increased susceptibility to hydrogen cracking. One way to solve this problem is to use solid state friction...
متن کاملEffect of Heat Input on Microstructure and Mechanical Properties in Friction Stir Welding of HSLA-60
High-strength low alloy steels are a class of steels used in applications that require high strength and good weldability, including ship hulls, gas pipelines and oil industry. One way to build parts is fusion welding that create areas with a large grain size in the heat-affected zone and increased susceptibility to hydrogen cracking. One way to solve this problem is to use solid state friction...
متن کاملMechanical behaviour of a new automotive high manganese TWIP steel in the presence of liquid zinc
iii Abstract: High manganese TWIP (TWinning Induced Plasticity) steels are particularly attractive for automotive applications because of their exceptional properties of strength combined with an excellent ductility. However, as austenitic steels, they appear to be sensitive to liquid zinc embrittlement during welding, the liquid zinc arising from the melted coating due to the high temperatures...
متن کامل